Heat/acoustic wave conversion component and heat/acoustic wave conversion unit

ABSTRACT

A heat/acoustic wave conversion component includes a partition wall that defines a plurality of cells, inside of the cells being filled with fluid that oscillates to transmit acoustic waves, the heat/acoustic wave conversion component mutually converting heat exchanged between the partition wall and the fluid and energy of acoustic waves resulting from oscillations of the fluid. The plurality of cells have an average of hydraulic diameters HDs that is 0.4 mm or less in a plane perpendicular to the cell extending direction, the heat/acoustic wave conversion component has an open frontal area at each end face of 60% or more and 93% or less, and distribution of hydraulic diameters HDs of the plurality of cells has relative standard deviation that is 2% or more and 30% or less.

The present application is an application based on JP 2014-192023 filedon Sep. 19, 2014 with Japan Patent Office, the entire contents of whichare incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to heat/acoustic wave conversioncomponents and heat/acoustic wave conversion units. More particularly,the present invention relates to a heat/acoustic wave conversioncomponent to convert heat and acoustic-wave energy mutually, and aheat/acoustic wave conversion unit including a heat/acoustic waveconversion component and a heat exchanger.

2. Description of the Related Art

Recently society as a whole has been becoming more and more interestedin effective use of energy resources, and so various techniques to reuseenergy have been developed on a trial basis. Among them, an energyrecycling system attracts attention because the acquisition rate (energyefficiency) of the energy acquired is high. The energy recycling systemconverts heat of high-temperature fluid, such as exhaust gas fromautomobiles, to acoustic-wave energy by a thermoacoustic effect, andfinally outputs such energy in the form of electric power. Variousefforts have been made toward the practical use of such a system.

Simply speaking, a thermoacoustic effect is a phenomenon to generateacoustic waves using heat. More specifically, the thermoacoustic effectis a phenomenon to oscillate an acoustic-wave transmitting medium in thethin tube to generate acoustic waves when heat is applied to one endpart of a thin tube to form a temperature gradient at the thin tube.Since it is effective to generate acoustic waves using a large number ofsuch thin tubes at one time, a honeycomb structure including a largenumber of through holes each having a small diameter is often used as acollective form of the thin tubes causing a thermoacoustic effect (seee.g., Patent Documents 1 to 3).

Meanwhile the honeycomb structure itself has been used for variouspurposes, without reference to the thermoacoustic effect, because of itsthree-dimensional geometry having a large surface area. For instance, atypical example is a honeycomb structure to load catalyst for exhaustpurification to remove fine particles from exhaust gas of automobiles,and various types of structures have been developed conventionally.Another example is a honeycomb structure having small through holes of afew tens to a few hundreds μm in diameter, which is developed as an ioncatalyst (see Non-Patent Documents 1, 2, for example). They aremanufactured by a chemical method solely, which is totally differentfrom extrusion that is typically used for honeycomb structures asfilters.

In this way, although honeycomb structures have been well knownconventionally, they are required to have specific properties to besuitable for a thermoacoustic effect when these structures are used asheat/acoustic wave conversion components to exert the thermoacousticeffect. For example, in order to exert a high thermoacoustic effect, thethrough holes preferably have a small diameter, and Patent Document 3proposes a honeycomb structure for a thermoacoustic effect, includingthrough holes having a diameter of 0.5 mm or more and less 1.0 mm thatis smaller than that of honeycomb structures to load catalyst forexhaust purification. Although the honeycomb structures in Non-PatentDocuments 1 and 2 have a very small pore diameter, they are manufacturedby a chemical method solely, and so they have limited lengths anddurability and so are not suitable for the honeycomb structure for athermoacoustic effect very much. On the other hand, the honeycombstructure for a thermoacoustic effect of Patent Document 3 satisfies anecessary condition that is durable in the use as a heat/acoustic waveconversion component to exert a thermoacoustic effect, and then has theadvantage of having an excellent heat/acoustic wave conversion function.

-   [Patent Document 1] JP-A-2005-180294-   [Patent Document 2] JP-A-2012-112621-   [Patent Document 3] JP-A-2012-237295-   [Non-Patent Document 1] URL:    http://www.mesl.t.u-tokyo.ac.jp/ja/research/tpv.html on the Internet-   [Non-Patent Document 2] URL:    http://www.ricoh.com/ja/technology/tech/009_honeycomb.html on the    Internet

SUMMARY OF THE INVENTION

Patent Document 3, however, does not consider very much a configurationof the honeycomb structure to make smaller a critical temperaturedifference at which acoustic waves start to be generated when thetemperature difference at both end parts of the honeycomb structure isbeing increased gradually. Thus, in Patent Document 3, startability toconvert heat/acoustic waves of a heat/acoustic wave conversion componentis low. In this way, honeycomb structures, to be used as a heat/acousticwave conversion component, have to be improved more.

In view of the above-mentioned circumstances, the present invention aimsto provide a heat/acoustic wave conversion component having a honeycombstructure and with improved startability to convert heat/acoustic waves,and a heat/acoustic wave conversion unit including such a heat/acousticwave conversion component and a heat exchanger.

To fulfill the above-mentioned object, the present invention providesthe following heat/acoustic wave conversion component and heat/acousticwave conversion unit.

[1] A heat/acoustic wave conversion component having a first end faceand a second end face, including a partition wall that defines aplurality of cells extending from the first end face to the second endface, inside of the cells being filled with fluid that oscillates totransmit acoustic waves, the heat/acoustic wave conversion componentmutually converting heat exchanged between the partition wall and thefluid and energy of acoustic waves resulting from oscillations of thefluid, wherein the plurality of cells have an average of hydraulicdiameters HDs that is 0.4 mm or less, where each hydraulic diameter HDis defined as HD=4×S/C, where S denotes an area of a cross-section ofeach cell in a plane perpendicular to the cell extending direction and Cdenotes a perimeter of the cross section, the heat/acoustic waveconversion component has an open frontal area at each end face of 60% ormore and 93% or less, and the plurality of cells have hydraulicdiameters HDs thereof which are different in accordance with each cell,and distribution of hydraulic diameters HDs of the plurality of cellshas relative standard deviation that is 2% or more and 30% or less.

[2] The heat/acoustic wave conversion component according to [1],wherein pairs of mutually neighboring cells of the plurality of cellshave thickness of the partition wall between neighboring cells of eachpair which is different in accordance with each neighboring cells, anddistribution of thickness of the partition wall between the neighboringcells has relative standard deviation that is 3% or more and 22% orless.

[3] The heat/acoustic wave conversion component according to [1] or [2],further including a circumferential wall that surrounds acircumferential face of the partition wall as a whole that defines theplurality of cells, wherein when the cross section of the heat/acousticwave conversion component in the plane is divided into a plurality ofunit segments each of which is a rectangular region of 1 mm in lengthand 1 mm in width, inside unit segments, which are remaining unitsegments obtained by removing unit segments including the cross sectionof the circumferential wall from the plurality of unit segments, haveopen frontal areas of the cells therein which are different inaccordance with each inside unit segment, and distribution of openfrontal areas of the cells in the inside unit segments has relativestandard deviation of 7% or more and 40% or less.

[4] A heat/acoustic wave conversion unit, comprising the heat/acousticwave conversion component according to any one of [1] to [3], in a statewhere inside of the plurality of cells is filled with the fluid, whenthere is a temperature difference between a first end part on the firstend face side and a second end part on the second end face side, theheat/acoustic wave conversion component oscillating the fluid along theextending direction in accordance with the temperature difference andgenerating acoustic waves; and

a pair of heat exchangers that are disposed in a vicinity of the firstend part and the second end part of the heat/acoustic wave conversioncomponent, respectively, the heat exchangers exchanging heat with theboth end parts to give a temperature difference between the both endparts.

[5] A heat/acoustic wave conversion unit including the heat/acousticwave conversion component according to any one of [1] to [3], in a statewhere inside of the plurality of cells is filled with the fluid, andwhen the fluid oscillates along the extending direction while receivingacoustic waves transmitted, the heat/acoustic wave conversion componentgenerating a temperature difference between a first end part on thefirst end face side and a second end part on the second end face side inaccordance with oscillations of the fluid; a heat exchanger that isdisposed in a vicinity of one of the first end part and the second endpart of the heat/acoustic wave conversion component, the heat exchangersupplying heat to the one end part or absorbing heat from the one endpart to keep a temperature at the one end part constant; and a hotheat/cold heat output unit that is disposed in a vicinity of the otherend part of the first end part and the second end part of theheat/acoustic wave conversion component that is on the opposite side ofthe one end part, the hot heat/cold heat output unit outputting hot heator cold heat obtained from exchanging of heat with the other end part sothat, in a state where the temperature of the one end part is keptconstant by the heat exchanger and when the heat/acoustic waveconversion component receives acoustic waves transmitted, the other endpart has a temperature difference in accordance with oscillations of thefluid due to transmission of the acoustic waves with reference to theone end part kept at the constant temperature. Here, “outputting hotheat or cold heat” means, for example, “outputting fluid whosetemperature is increased or fluid whose temperature is decreased”.

Since the heat/acoustic wave conversion component of the presentinvention has a hydraulic diameter HD of 0.4 mm or less and open frontalarea of 60% or more and 93% or less, it can keep sufficient energyconversion efficiency to convert heat into acoustic wave energy by athermoacoustic effect, and includes distribution of hydraulic diametersHDs of the plurality of cells has relative standard deviation that is 2%or more and 30% or less so as to improve the startability ofheat/acoustic wave conversion.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 schematically shows the configuration of a power generationsystem, to which one embodiment of a heat/acoustic wave conversion unitand a heat/acoustic wave conversion component of the present inventionis applied.

FIG. 2 schematically shows a cold heat generation system, to which theheat/acoustic wave conversion unit and the heat/acoustic wave conversioncomponent in FIG. 1 are applied.

FIG. 3 schematically shows the configuration of the heat/acoustic waveconversion unit of FIG. 1.

FIG. 4 is a perspective view showing the appearance of thehigh-temperature side heat exchanger in the heat/acoustic waveconversion unit of FIG. 3.

FIG. 5 is a cross-sectional view of the high-temperature side heatexchanger when viewing an inflow port and an outflow port of thehigh-temperature side annular tube in a plane.

FIG. 6 schematically shows one form of a heat/acoustic wave conversionunit including another honeycomb structure fitted in thehigh-temperature side annular tube.

FIG. 7 is a schematic cross-sectional view of the high-temperature sideheat exchanger taken along the line A-A of FIG. 6.

FIG. 8 schematically shows another form of the heat/acoustic waveconversion unit of the present invention that is different from theheat/acoustic wave conversion units in FIGS. 6 and 7.

FIG. 9 schematically shows still another form of the heat/acoustic waveconversion unit that is different from the heat/acoustic wave conversionunit in FIG. 8.

FIG. 10 is a cross-sectional view of a high-temperature side heatexchanger having a mesh structure.

FIG. 11A is a cross-sectional view of the heat/acoustic wave conversioncomponent of FIG. 3 in a plane perpendicular to the penetratingdirection of the cells of the heat/acoustic wave conversion component.

FIG. 11B is a conceptual diagram showing division of a cross section ofa heat/acoustic wave conversion component using unit segments.

FIG. 12 is a perspective view showing the appearance of a die that isused to prepare a honeycomb formed body in the present embodiment.

FIG. 13 is a perspective view showing the appearance of the die in FIG.12 that is viewed from the opposite side of FIG. 12.

FIG. 14 is an enlarged plan view showing a part of the surface of thedie in FIG. 12.

FIG. 15 schematically shows a cross section of the die of FIG. 14 takenalong the line A-A′.

FIG. 16 shows an example of the retainer plate configuration.

FIG. 17 shows another example of the retainer plate configuration thatis different from FIG. 16.

FIG. 18 shows still another example of the retainer plate configuration.

FIG. 19 shows a further example of the retainer plate configuration thatis different from FIG. 18.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The following describes embodiments of the present invention, withreference to the drawings. The present invention is not limited to thefollowing embodiments, and is to be understood to include the followingembodiments, to which modifications and improvements are added as neededbased on the ordinary knowledge of a person skilled in the art withoutdeparting from the scope of the present invention.

FIG. 1 schematically shows the configuration of a power generationsystem, to which one embodiment of a heat/acoustic wave conversion unitand a heat/acoustic wave conversion component of the present inventionis applied.

A power generation system 1000 in FIG. 1 includes a heat/acoustic waveconversion unit 100, a looped tube 4, a resonant tube 5 and an energyconverter 6.

The looped tube 4 is a loop-shaped tube that is connected to an end onthe upper side (upper end) and an end on the lower side (lower end) inthe drawing of the heat/acoustic wave conversion unit 100. The resonanttube 5 is a straight tube, having one end connected to the looped tube 4and the other end connected to the energy converter 6. Herein theresonant tube 5 and the energy converter 6 as a whole makes up a tubethat is substantially closed in the end on the right side of thedrawing.

The heat/acoustic wave conversion unit 100 includes a heat/acoustic waveconversion component 1, a high-temperature side heat exchanger 2 and alow-temperature side heat exchanger 3.

The high-temperature side heat exchanger 2 receives the inflow of heatedfluid at high temperatures (e.g., high-temperature exhaust gas), andtransmits the heat thereof to the lower end of the heat/acoustic waveconversion component 1 of FIG. 1 to let the heated fluid having atemperature lower than that at the time of inflow flow out. On the otherhand, the low-temperature side heat exchanger 3 receives the inflow ofcooled fluid (e.g., water) at relatively low temperatures compared withthe heated fluid flowing in the high-temperature side heat exchanger 2and transmits the cold heat to the upper end of the heat/acoustic waveconversion component 1 of FIG. 1 to let the cooled fluid having atemperature higher than that at the inflow flow out. Such functions ofthe high-temperature side heat exchanger 2 and the low-temperature sideheat exchanger 3 yield the state where the lower end of theheat/acoustic wave conversion component 1 has a relatively highertemperature than at the upper end. The heat/acoustic wave conversioncomponent 1 has a honeycomb structure including a plurality of throughholes (hereinafter called cells) like thin tubes that are elongatedvertically in the drawing. Each cell is partitioned from the neighboringcells by a partition wall, and is in communication with the looped tube4 via the high-temperature side heat exchanger 2 and the low-temperatureside heat exchanger 3.

Herein the looped tube 4, the resonant tube 5 and each cell of theheat/acoustic wave conversion component 1 are internally filled withworking fluid that generates oscillations of longitudinal waves andtransmits acoustic waves. An example of the working fluid includes gashaving low viscosity and being less reactive, such as rare gas.

In such a heat/acoustic wave conversion component 1, when there is atemperature difference as stated above at the both ends, the workingfluid in each cell starts to oscillate in the penetrating direction ofthe cells. Then the oscillations are transmitted as acoustic wavesexternally from the heat/acoustic wave conversion component 1. Such aphenomenon of the working fluid oscillating in response to the giventemperature difference is called self-induced oscillations, and is aconventionally well-known phenomenon that occurs when a temperaturegradient is given to a thin tube. A thermoacoustic effect refers togeneration of acoustic waves due to the self-induced oscillation ofworking fluid resulting from heat. The following briefly describes thisself-induced oscillation (a lot of documents describe the details, andPatent Document 3 also provides the detailed descriptions thereon, forexample).

When giving a temperature gradient to a thin tube, then working fluidinside of the thin tube on the high-temperature side absorbs heat fromthe wall surface of the tube and expands from the high-temperature sideto the low-temperature side. Then, the working fluid releases heat tothe wall surface on the low-temperature side and is compressed, and thenreturns back to the high-temperature side. Such exchange of heat withthe wall surface and expansion/compression are repeated, which resultsin oscillation of the working fluid in the elongation direction of thetube. Simply speaking, such motion of the working fluid can said to bethe motion to convey heat so as to alleviate (weaken) the temperaturegradient at the wall surface. As can be clear from this description aswell, such a phenomenon occurs only when the tube is so thin that thethermal effects from the wall surface are large on the working fluidinside. That is, as the tube is made thicker, the thermal effect fromthe wall surface decreases (i.e., it becomes closer to an adiabaticstate), and so such self-induced oscillation hardly occurs. Then, thethickness of the tube is an important factor to generate acoustic wavesby the self-induced oscillation, and the thickness of the tube can beevaluated more quantitatively based on a hydraulic diameter HD that isdefined as HD=4×S/C, where S denotes the cross-sectional area of thetube and C denotes the perimeter of this section.

Referring back to FIG. 1, the power generation system 1000 is describedbelow again.

Since the heat/acoustic wave conversion component 1 includes a pluralityof cells like thin tubes and the self-induced oscillation occurs in eachcell, acoustic waves as the collection of oscillations of the workingfluid in these plurality of cells are then issued from the heat/acousticwave conversion component 1 to the looped tube 4. Then such acousticwaves are transmitted through the looped tube 4 in the direction of thedotted arrows in the drawing. Most of the acoustic waves transmittedthrough the looped tube 4 travels in the resonant tube 5 to the right inthe drawing. As described above, the resonant tube 5 and the energyconverter 6 as a whole makes up a tube that is substantially closed inthe end on the right side of the drawing, and so some of the acousticwaves are reflected and travel to the left in the opposite direction inthe drawing. Then, both of these traveling waves are overlapped in theresonant tube 5. At this time, if the frequency of the traveling wavesmatches with the resonant frequency that is determined, for example, bythe length of the resonant tube 5 then so-called resonance occurs in theresonant tube 5, and steady waves are generated, which are overlappedwaves of both of these traveling waves and have the resonant frequency.In the drawing, the double-headed arrow in the dashed-dotted lineindicates the presence of the steady waves.

Herein the energy converter 6 is equipped with a mechanism not shownthat is capable of changing the effective length of the resonant tube 5,which can adjust the resonance frequency so as to cause the resonance.An exemplary mechanism to change the effective length of the resonanttube 5 includes one described in Patent Document 1, for example.Although the following describes the case where the effective length ofthe resonant tube 5 can be changed, in the power generation system 1000of FIG. 1, a dominant frequency component of the frequency components ofacoustic waves generated at the heat/acoustic wave conversion component1 and traveling through the looped tube 4 may be determined beforehand,and the length of the resonant tube 5 may be configured beforehand to bea special length which makes the frequency of the dominant frequencycomponent the resonance frequency.

The energy converter 6 is equipped with a mechanism to convert acousticwaves into electrical signals as well. An exemplary conversion mechanismof such a type includes a mechanism equipped with a microphone asdescribed in Patent Document 1. Although the conversion mechanismincluding a microphone is the simplest one, the conversion mechanism isnot limited to such a mechanism including a microphone. For instance,conventionally known various mechanisms (e.g., the mechanism of PatentDocument 2), which is to convert acoustic-wave energy to mechanicalenergy and then convert such mechanical energy to electric power byelectromagnetic induction, can be used.

With the configuration as stated above, the power generation system 1000of FIG. 1 can convert heat of high-temperature heated fluid (e.g.,high-temperature exhaust gas) flowing into the high-temperature sideheat exchanger 2 into electric power, and so enables effective use(recycling) of energy.

Next the following describes a cold heat generation system, to which theheat/acoustic wave conversion unit 100 and the heat/acoustic waveconversion component 1 as stated above are applied.

FIG. 2 schematically shows a cold heat generation system, to which theheat/acoustic wave conversion unit 100 and the heat/acoustic waveconversion component 1 in FIG. 1 are applied.

A cold heat generation system 2000 in FIG. 2 includes a looped tube 4′,a transmission tube 5′, an acoustic-wave generation part 7, and theheat/acoustic wave conversion unit 100 described referring to FIG. 1.

The looped tube 4′ is a loop-shaped tube that is connected to an end onthe upper side (upper end) and an end on the lower side (lower end) ofthe heat/acoustic wave conversion unit 100 in FIG. 2, and is incommunication with the plurality of cells of the heat/acoustic waveconversion component 1 via the high-temperature side heat exchanger 2and the low-temperature side heat exchanger 3. The transmission tube 5′is a straight tube, having one end connected to the looped tube 4′ andthe other end connected to the acoustic-wave generation part 7. Theacoustic-wave generation part 7 has a function of generating acousticwaves, and an example of the acoustic-wave generation part 7 includes aspeaker that receives electric power and outputs acoustic waves. Anotherexample is a system that is obtained by removing the energy converter 6from the power generation system 1000 in FIG. 1 and that receives heatand generates acoustic waves (in this case, the resonant tube 5 on theright side is an open end where no reflections occur, and so unlike thestate of FIG. 1, traveling waves toward right are transmitted in theresonant tube 5).

Although the heat/acoustic wave conversion unit 100 has the sameconfiguration as that described with reference to FIG. 1, it isconfigured so that, unlike FIG. 1, cooled fluid (e.g., water), which issimilar to the cooled fluid flowing into the low-temperature side heatexchanger 3 in FIG. 1, flows into both of the high-temperature side heatexchanger 2 and the low-temperature side heat exchanger 3 of FIG. 2.

Herein the looped tube 4′, the transmission tube 5′ and each cell of theheat/acoustic wave conversion component 1 are internally filled withworking fluid that generates oscillations of longitudinal waves andtransmits acoustic waves. Working fluid similar to that used in thepower generation system 1000 of FIG. 1 can be used.

Acoustic waves generated at the acoustic-wave generation part 7 aretransmitted through the transmission tube 5′ in the direction of thedashed-dotted arrow in FIG. 2, and then are transmitted through thelooped tube 4′ in the direction of the dashed line arrow in FIG. 2.Then, the acoustic waves reach the heat/acoustic wave conversion unit100, and travel in each cell from the upper side in FIG. 2 of theheat/acoustic wave conversion component 1. At this time, due to heattransport by acoustic waves, the system can have a state where the endon the high-temperature side heat exchanger 2 side has a relativelyhigher in temperature than the end on the low-temperature side heatexchanger 3 side. At the high-temperature side heat exchanger 2, cooledfluid close to the ambient temperature flows in, and the fluid at atemperature higher than the ambient temperature flows out. On the otherhand, since heat is transported to the end on the high-temperature sideheat exchanger 2 side due to heat transport by acoustic waves, the endof the heat/acoustic wave conversion component 1 on the low-temperatureside heat exchanger 3 side has a temperature lower than the ambienttemperature. Then at the low-temperature side heat exchanger 3, cooledfluid close to the ambient temperature flows in, and the fluid at atemperature lower than the ambient temperature flows out because heat istaken by the end of the heat/acoustic wave conversion component 1 on thelow-temperature side heat exchanger 3 side. In other words, cold heat isoutput in the form of cold water.

With the configuration as stated above, the cold heat generation system2000 in FIG. 2 can output cold heat using acoustic-wave energy generatedat the acoustic-wave generation part 7. Especially when it includes, asthe acoustic-wave generation part 7, the system corresponding to thepower generation system 1000 of FIG. 1 other than the energy converter6, high-temperature heated fluid (e.g., high-temperature exhaust gas)flowing into the high-temperature side heat exchanger 2 of FIG. 1 can beconverted into cold heat, which then enables effective use (recycling)of energy.

As stated above, in the power generation system 1000 in FIG. 1 and thecold heat generation system 2000 in FIG. 2, the heat/acoustic waveconversion unit 100 that is one embodiment of the present inventionplays a very important role. Then the following describes theheat/acoustic wave conversion unit 100 in more details, by way of anexemplary situation where that is used in the power generation system1000 of FIG. 1. The following describes the power generation system 1000of FIG. 1, by way of an example where high-temperature heated fluid(e.g., exhaust gas itself) at about 400 to 600° C. that are typicaltemperatures of the exhaust gas from automobiles flows in thehigh-temperature side heat exchanger 2 of FIG. 1, and low-temperaturecooled fluid (e.g., water) at about 20 to 70° C. flows into thelow-temperature side heat exchanger 3. In this case, a temperaturedifference between both ends of the heat/acoustic wave conversioncomponent 1 is about 330 to 580° C.

Naturally the properties of the heat/acoustic wave conversion unit 100described below are the same as in the case where it is used in the coldheat generation system 2000 of FIG. 2 as well.

FIG. 3 schematically shows the configuration of the heat/acoustic waveconversion unit 100 of FIG. 1.

The heat/acoustic wave conversion unit 100 includes a heat/acoustic waveconversion component 1, a high-temperature side heat exchanger 2 and alow-temperature side heat exchanger 3 as well as a metal member 32 andan interference member 1 a. These components as a whole are stored in ahousing 100 a and are connected to a looped tube 4 (see FIG. 1 also).

The heat/acoustic wave conversion component 1 has a honeycomb structurein which a plurality of cells 14, each being a thin-tube like throughhole, are partitioned and defined by a partition wall 11. Herein, theword “cell” in the present specification refers to a through hole onlythat does not include the partition wall. Each cell 14 has a penetratingdirection (an extending direction in which each cell 14 extends) that isthe vertical direction of FIG. 3, and is open at both end faces of anend face on the low-temperature side heat exchanger 3 side and an endface of the high-temperature side heat exchanger 2 side. The end face ofthe heat/acoustic wave conversion component 1 on the low-temperatureside heat exchanger 3 side is in contact with the metal member 32, andis opposed to the low-temperature side heat exchanger 3 with the metalmember 32 disposed therebetween. Although the metal member 32 isdisposed in this case, the present invention may have a form without themetal member 32. When the metal member 32 is omitted, working fluid incontact with a mesh lamination body 30 described later is cooled, andthen the cooled working fluid comes into contact with the vicinity ofthe end face of the heat/acoustic wave conversion component 1 due to thedisplacement of the working fluid, which corresponds to oscillations ofacoustic waves, and cools the vicinity of the end face. When the metalmember 32 is omitted, a gap between the heat/acoustic wave conversioncomponent 1 and the low-temperature side heat exchanger 3 is as small aspossible preferably.

The metal member 32 is a metal member having a plate shape, at a centerpart of which a plurality of parallel slits (not shown) are formed, andFIG. 3 shows only a side-face part (thickness part) of the plate shape.

The low-temperature side heat exchanger 3 includes the mesh laminationbody 30 including a plurality of metal mesh plates (e.g., made ofcopper). The low-temperature side heat exchanger 3 includes alow-temperature side annular tube 31 also that is an annular tubesurrounding the side face of the mesh lamination body 30. FIG. 3schematically shows the state where such a low-temperature side annulartube 31 surrounding the side face of the mesh lamination body 30sandwiches the mesh lamination body 30 from both sides at across-section including an inflow port 31 a and an outflow port 31 b.This low-temperature side annular tube 31 has a function of receiving,from the inflow port 31 a, the inflow of cooled fluid (e.g., water) thatis at a relatively low temperature with reference to the heated fluidflowing into the high-temperature side heat exchanger 2 described later,and transmitting cold heat of the cooled fluid to the mesh laminationbody 30 (in other words, transmits heat at the mesh lamination body 30to the cooled fluid) and letting cooled fluid with an increasedtemperature flow out from the outflow port 31 b.

Cold heat transmitted to the mesh lamination body 30 is transmitted tothe working fluid in contact therewith, and is then transmitted to theend face of the heat/acoustic wave conversion component 1 on thelow-temperature side heat exchanger 3 side due to displacement ofacoustic waves to cool the end of the heat/acoustic wave conversioncomponent 1 on the low-temperature side heat exchanger 3 side. To thisend, the metal member 32 is preferably made of a material having largeheat conductivity, which may be made of e.g., copper.

That is the detailed description of the configuration of thelow-temperature side heat exchanger 3, and the heat/acoustic waveconversion unit of the present invention is not limited especially aboutthe details of the low-temperature side heat exchanger, and aconventionally known heat exchanger may be used. The same configurationas that of the high-temperature side heat exchanger 2 described latermay be used.

The side face of the heat/acoustic wave conversion component 1 issurrounded by the interference member 1 a, and FIG. 3 schematicallyshows the cross section of the surrounding interference member 1 a astwo parts that sandwich the heat/acoustic wave conversion component 1from both of right and left sides in the drawing. This interferencemember 1 a has a function as a thermal insulator to avoid heattransmission between the ends of the heat/acoustic wave conversioncomponent 1 on the low-temperature side heat exchanger 3 side and on thehigh-temperature side heat exchanger 2 side via the surroundingenvironment outside of the heat/acoustic wave conversion component 1.

The high-temperature side heat exchanger 2 includes a heat-exchanginghoneycomb structure 20 and a high-temperature side annular tube 21. Theheat-exchanging honeycomb structure 20 has a honeycomb structuresimilarly to the heat/acoustic wave conversion component 1, includingtwo or more cells 20 d, each being a thin-tube like through holepenetrating vertically in FIG. 3, that are partitioned and defined by apartition wall 20 a. The high-temperature side annular tube 21 is anannular tube surrounding the side face of the heat-exchanging honeycombstructure 20, and has a function of receiving, from an inflow port 21 a,the inflow of high-temperature heated fluid (e.g., high-temperatureexhaust gas), transmitting heat of the heated fluid to theheat-exchanging honeycomb structure 20 and letting heated fluid with adecreased temperature flow out from an outflow port 21 b. Then as shownin FIG. 3, the high-temperature side annular tube 21 internally includesa metal or ceramic fin 21 e containing SiC (silicon carbide) as a maincomponent to increase the contact area with the heated fluid.

FIG. 4 is a perspective view showing the appearance of thehigh-temperature side heat exchanger 2 in the heat/acoustic waveconversion unit 100 of FIG. 3, and FIG. 5 is a cross-sectional view ofthe high-temperature side heat exchanger 2, which is a plan viewincluding the inflow port 21 a and the outflow port 21 b of thehigh-temperature side annular tube 21.

As shown in FIG. 4, the high-temperature side heat exchanger 2 includesthe heat-exchanging honeycomb structure 20 that is fitted in a centerhollow part of the annular shape of the high-temperature side annulartube 21. As indicated with thick arrows in FIG. 4, high-temperatureheated fluid (e.g., high-temperature exhaust gas) flows into thehigh-temperature side annular tube 21 from the inflow port 21 a on thelower side of the drawing and flows out from the outflow port 21 b onthe upper side of the drawing. At this time, as indicated with thearrows in FIG. 5, the high-temperature heated fluid flowing in throughthe inflow port 21 a directly hits a circumferential wall 20 b definingthe circular circumference of the heat-exchanging honeycomb structure 20and then is branched off into left and right two sides of thecircumferential wall 20 b and travels along the circumferential wall 20b. Then they join together at the outflow port 21 b to flow out. In thisway, the high-temperature heated fluid directly comes into contact withthe circumferential wall 20 b of the heat-exchanging honeycomb structure20, whereby a lot of heat is directly transmitted from thehigh-temperature heated fluid to the circumferential wall 20 b, and suchheat is transmitted to the partition wall 20 a in the heat-exchanginghoneycomb structure 20 and the working fluid inside of the cells 20 d aswell. In this way, the heat-exchanging honeycomb structure 20 candirectly come into contact with the high-temperature heated fluidbecause the heat-exchanging honeycomb structure 20 is made of a materialhaving high heat resistance and good heat conductivity as describedlater, and such a direct contact with the heated fluid can suppress heatloss and improve heat-exchanging efficiency as compared with the caseincluding another member intervening therebetween.

Although it is preferable that the heat-exchanging honeycomb structure20 directly comes into contact with heated fluid in this way, thepresent invention may have a form in which, instead of such a directcontact of the circumferential wall 20 b of the heat-exchanginghoneycomb structure 20 with high-temperature heated fluid, thecircumferential wall 20 b is surrounded with metal. Especially whenhigh-pressure gas (e.g., inert rare gas such as argon) is used as theworking fluid to transmit acoustic waves, it is preferable to surroundthe circumferential wall 20 b with metal from the viewpoint ofhermetically sealing of such high-pressure gas and avoiding the leakage.In this case, the metal surrounding the circumferential wall 20 b has acircumferential face, on which a metal fin (see fin 21 e in FIG. 3, forexample) is preferably provided so as to protrude in the outwarddirection (radial direction) from the center of the heat-exchanginghoneycomb structure 20 of FIG. 5. This is to increase the contact areawith the high-temperature heated fluid and improve heat-exchangingefficiency. If the contact area with the high-temperature heated fluidis small, exchange of heat between the high-temperature heated fluid andthe high-temperature side heat exchanger 2 is not sufficient, and so theheat-exchanging efficiency of the high-temperature side heat exchanger 2deteriorates. In this way, it is important for the high-temperature sideheat exchanger 2 to maximize the contact area with the high-temperatureheated fluid.

In a most preferable form, another honeycomb structure made of a ceramicmaterial containing SiC (silicon carbide) as a main component is fittedin the tube of the high-temperature side annular tube. This is becausesuch a ceramic material containing SiC (silicon carbide) as a maincomponent has higher heat conductivity at high temperatures than that ofmetal fins, and the contact area with high-temperature gas also can beincreased dramatically. Further, this can avoid a problem of erosion anddeterioration due to high-temperature heated fluid, which can be aproblem for metal fins. The following describes such a preferable form.

FIG. 6 schematically shows one form of a heat/acoustic wave conversionunit including another honeycomb structure fitted in thehigh-temperature side annular tube. FIG. 7 is a schematiccross-sectional view of the high-temperature side heat exchanger takenalong the line A-A of FIG. 6.

In FIGS. 6 and 7, the same reference numerals are assigned to the sameelements as those in FIGS. 3 to 5, and their duplicated descriptions areomitted.

A high-temperature side heat exchanger 2′ in a heat/acoustic waveconversion unit 200 in FIG. 6 includes a heat-exchanging honeycombstructure 20′ and two mutually different high-temperature side annulartubes 211 and 212. The heat-exchanging honeycomb structure 20′ has ahoneycomb structure including two or more cells penetrating horizontallyin the drawing that are partitioned and defined by a partition wall, andtransmits heat transmitted from heated fluid via the two differenthigh-temperature side annular tubes 211 and 212 to the heat/acousticwave conversion component 1. Herein, the heat-exchanging honeycombstructure 20′ is disposed with a distance t from the heat/acoustic waveconversion component 1.

As shown in FIG. 7, the two high-temperature side annular tubes 211 and212 internally include in-tube honeycomb structures 2110 and 2120,respectively, made of a ceramic material containing SiC (siliconcarbide) as a main component. These in-tube honeycomb structures 2110and 2120 both have a honeycomb structure including two or more cellspenetrating horizontally in the drawing that are partitioned and definedby a partition wall. As shown in the arrows of the drawing, heated fluidflowing in the two high-temperature side annular tubes 211 and 212passes through each cell of the in-tube honeycomb structures 2110 and2120, and then flows out. At this time, heat of the heated fluid passingthrough each cell is transmitted to the in-tube honeycomb structures2110 and 2120, and such heat is then transmitted to the heat-exchanginghoneycomb structure 20′ via the wall faces of the high-temperature sideannular tubes 211, 212 and a metal tube (not shown) surrounding the sideface (face of the circumferential wall) of the heat-exchanging honeycombstructure 20′. Although FIG. 7 shows the cross-section of theheat-exchanging honeycomb structure 20′ as a rectangular shape forsimplicity, it may have a circular cross section as in FIGS. 4 and 5,and a substantially similar configuration can be realized when thehigh-temperature side annular tubes 211 and 212 have a shape along thecircle.

In this way, the circumferential wall of the heat-exchanging honeycombstructure 20′ is surrounded with a metal tube, on an outside of whichthe two in-tube honeycomb structures 2110 and 2120 made of a ceramicmaterial containing SiC (silicon carbide) as a main component aredisposed. In this configuration, the heat-exchanging honeycomb structure20′ is not in a direct contact with the heated fluid, and so erosion anddeterioration due to high-temperature heated fluid can be suppressed.When inert rare gas (e.g., argon) is used as the working fluid, aproblem of erosion of the heat-exchanging honeycomb structure 20′ due toworking fluid does not happen. In this case, the heat-exchanginghoneycomb structure 20′ may be made of a metal material having good heatconductivity, such as copper, as well as a ceramic material containingSiC (silicon carbide) as a main component.

Herein, the heat-exchanging honeycomb structure 20′ in FIG. 6 preferablyhas a length L′ of the order of wavelength of acoustic waves generatedfrom oscillations of the working fluid. If the length L′ is too longwith reference to the wavelength of acoustic waves, the heat given tothe working fluid (e.g., inert rare gas) will be insufficient. If thelength L′ is too short with reference to the wavelength of acousticwaves, then working fluid may pass through the heat-exchanging honeycombstructure 20′ from the outside and reach the heat/acoustic waveconversion component 1, and the working fluid at a relatively lowtemperature may cool the end of the heat/acoustic wave conversioncomponent 1 on the high-temperature side heat exchanger sideunfortunately.

FIG. 8 schematically shows another form of the heat/acoustic waveconversion unit of the present invention that is different from theheat/acoustic wave conversion units in FIGS. 6 and 7, and FIG. 9schematically shows still another form of the heat/acoustic waveconversion unit that is different from the heat/acoustic wave conversionunit in FIG. 8.

In the heat/acoustic wave conversion unit of FIG. 8, heated fluid flowsinto the high-temperature side heat exchanger 2A from the upper side ofthe drawing and flows through the high-temperature side heat exchanger2A, and then flows out toward the lower side of the drawing. On theother hand, in the heat/acoustic wave conversion unit of FIG. 9, heatedfluid flows into the high-temperature side heat exchanger 2A′ from theupper side of the drawing and flows through the high-temperature sideheat exchanger 2A′, and then flows out toward the upper side of thedrawing. Herein in both of the heat/acoustic wave conversion units ofFIGS. 8 and 9, cooled fluid flows into the low-temperature side heatexchanger 3A from the upper side of the drawing and flows through thelow-temperature side heat exchanger 3A, and then flows out toward theupper side of the drawing. FIGS. 8 and 9 show the configurationpartially as a perspective view to clarify the internal configurations(configuration including the following two honeycomb structures 22, 23).

The high-temperature side heat exchanger 2A in FIG. 8 and thehigh-temperature side heat exchanger 2A′ in FIG. 9 include apillar-shaped honeycomb structure 23 made of a metal material, and ahollow and round pillar-shaped (in other words, a cylindrical shapehaving a thickness) honeycomb structure 22 made of a ceramic materialcontaining SiC (silicon carbide) as a main component surrounding thehoneycomb structure. At the circumference of the honeycomb structure 23,a metal mesh outer tube 23 a described later, which is made of the samemetal material, is formed integrally with the metal honeycomb structure23. To be precise, a metalized layer, which is described later, ispresent between the two honeycomb structures 22 and 23. These twohoneycomb structures 22 and 23 both have a honeycomb structure includingtwo or more round pillar-shaped cells penetrating in the elongateddirection that are partitioned and defined by a partition wall. Such aconfiguration in FIGS. 8 and 9 also can suppress heat loss and improveheat conversion efficiency.

These embodiments have a honeycomb structure including the honeycombstructure 23 made of a metal material, and instead of this, a meshstructure made up of metal mesh may be used.

FIG. 10 is a cross-sectional view of a high-temperature side heatexchanger having a mesh structure.

The high-temperature side heat exchanger in FIG. 10 includes, inside ofthe honeycomb structure 22 made of a ceramic material containing SiC(silicon carbide) as a main component that is surrounded with a metalouter tube 22 a, a metal mesh member 23′ via a cylindrical metalizedlayer 23 b and a metal mesh outer tube 23 a. Herein the metalized layer23 b is a layer formed by baking of metal such as molybdenum andmanganese, which is a layer to bond the metal mesh outer tube 23 a madeof metal and the honeycomb structure 22 made of ceramic. Theconfiguration in FIG. 10 also can suppress heat loss and improveheat-exchanging efficiency.

Referring back to FIGS. 3 to 5 again, the descriptions are continued inthe following.

As shown in FIG. 3, the end face of the heat-exchanging honeycombstructure 20 on the heat/acoustic wave conversion component 1 side (theupper end face of the heat-exchanging honeycomb structure 20) is in adirect contact with the end face of the heat/acoustic wave conversioncomponent 1 on the high-temperature side heat exchanger 2 side (thelower end face of the heat/acoustic wave conversion component 1).Hereinafter this upper end face of the heat-exchanging honeycombstructure 20 is called a contact face 20 s. Instead of such a directcontact between the heat/acoustic wave conversion component 1 and theheat-exchanging honeycomb structure 20, gap t as in FIG. 6 may bepresent between the heat/acoustic wave conversion component 1 and theheat-exchanging honeycomb structure 20 in the present invention. In thiscase, heat transmitted to the heat-exchanging honeycomb structure 20 istransmitted to working fluid coming into contact with theheat-exchanging honeycomb structure 20, and the heated working fluidcomes into contact with the vicinity of the end face of theheat/acoustic wave conversion component 1 due to displacement of theworking fluid, which corresponds to oscillations of acoustic waves, toheat the vicinity of the end face. This allows the end of theheat/acoustic wave conversion component 1 on the high-temperature sideheat exchanger 2 side to keep a relatively high-temperature state ascompared with the end on the low-temperature side heat exchanger 3 side.

This heat-exchanging honeycomb structure 20 is made of a ceramicmaterial containing SiC (silicon carbide) as a main component. Since aceramic material has high heat resistance, such a material is suitablefor the material of the heat-exchanging honeycomb structure 20 thatdirectly comes into contact with high-temperature heated fluid as statedabove. Further, since a ceramic material containing SiC (siliconcarbide) as a main component has relatively good heat conductivity amongother ceramic materials, such a material is suitable for a function tolet the heat-exchanging honeycomb structure 20 transmit heat to theheat/acoustic wave conversion component 1 as stated above. Note herethat “containing SiC (silicon carbide) as a main component” means thatSiC accounts for 50 mass % or more of the material of theheat-exchanging honeycomb structure 20. At this time, the porosity ispreferably 0 to 10%. It is then preferable that the thickness of thepartition wall 20 a is 0.25 to 0.51 mm and the cell density is 15 to 62cells/cm².

Specific examples of the ceramic material containing SiC as a maincomponent include simple SiC as well as Si impregnated SiC, (Si+Al)impregnated SiC, metal composite SiC, recrystallized SiC, Si₃N₄ and SiC.Among them, Si impregnated SiC and (Si+Al) impregnated SiC arepreferable. This is because Si impregnated SiC has good heatconductivity and heat resistance, and has low porosity although it is aporous body and so is formed densely, and then it can realize relativelyhigh strength as compared with SiC without impregnated Si.

As shown in FIG. 5, the heat-exchanging honeycomb structure 20 has aconfiguration of the triangle cells 20 d that are arranged periodicallywith a period of a constant length in the plane perpendicular to thepenetrating direction of the cells 20 d. As described later, theheat/acoustic wave conversion component 1 to which heat is to betransmitted also has a similar configuration, and the period of thecells 20 d in the heat-exchanging honeycomb structure 20 is integralmultiples of 10 or more of the period of cells 14 in the heat/acousticwave conversion component 1. In this way, the cells 20 d of theheat-exchanging honeycomb structure 20 have the same shape as that ofthe cells 14 of the heat/acoustic wave conversion component 1 to whichheat is to be transmitted, and the period of the cells 20 d of theheat-exchanging honeycomb structure 20 is integral multiples of theperiod of the cells 14 of the heat/acoustic wave conversion component 1,whereby working fluid contained inside the cells 20 d of theheat-exchanging honeycomb structure 20 and the cells 14 of theheat/acoustic wave conversion component 1 can move smoothly. The periodof the cells of the heat-exchanging honeycomb structure 20 is largerthan the period of the cells of the heat/acoustic wave conversioncomponent 1 because the cells 14 of the heat/acoustic wave conversioncomponent 1 are required to be very thin through holes to causeself-induced oscillations as stated above. On the other hand, there isno such a request for the cells 20 d of the heat-exchanging honeycombstructure 20, and the heat-exchanging honeycomb structure 20 may play arole of heat exchange simply, and so the period of them is larger thanthe period of the cells 14 of the heat/acoustic wave conversioncomponent 1 by one digit (ten times) or more.

As shown in FIG. 3, the contact face 20 s of the heat-exchanginghoneycomb structure 20 with the heat/acoustic wave conversion component1 is displaced toward the heat/acoustic wave conversion component 1(upper side in the drawing) from a heat-receiving region 21 c where theheat-exchanging honeycomb structure 20 directly comes into contact withhigh-temperature heated fluid to receive heat therefrom, and so does notoverlap with the heat-receiving region 21 c. If the contact face 20 soverlaps with the heat-receiving region 21 c, a temperature may differgreatly between the periphery of an edge of the contact face 20 s closerto the heat-receiving region 21 c and a center region away from theheat-receiving region 21 c. In this case, the end (lower end in FIG. 3)of the heat/acoustic wave conversion component 1 on the heat-exchanginghoneycomb structure 20 side is not heated uniformly, and so the cells ofthe heat/acoustic wave conversion component 1 cause non-uniformself-induced oscillations unfortunately. The heat-exchanging honeycombstructure 20 in FIG. 3 is configured so as not to overlap the contactface 20 s with the heat-receiving region 21 c to avoid such a problem.

As shown in FIG. 5, the heat-exchanging honeycomb structure 20 includesa slit 20 c as a gap part of the circumferential wall 20 b, the slitextending in the penetrating direction of the cells 20 d. FIG. 5 showsthe example of slits 20 c formed at four positions of thecircumferential face of the heat-exchanging honeycomb structure 20. Suchslits 20 c can mitigate thermal stress applied to the circumferentialwall 20 b when high-temperature heated fluid directly comes into contactwith the circumferential wall 20 b, which then can suppress breakage orpeeling-off of the circumferential wall 20 b and the partition wall 20a.

As shown in FIG. 5, the high-temperature side annular tube 21 isprovided with four heat-resistant metal plates 21 d along the extendingdirection of the slits 20 c to fill the gaps at the slits 20 c andextend. These four heat-resistant metal plates 21 d can prevent workingfluid from leaking into the high-temperature side annular tube 21through the four slits 20 c. Note here that the heat-exchanginghoneycomb structure 20 is supported by fitting into these fourheat-resistant metal plates 21 d at an annular center part of thehigh-temperature side annular tube 21. These four heat-resistant metalplates 21 d are provided with fins 21 e (see FIG. 3 also) made of metalor ceramic containing SiC (silicon carbide) as a main component, thefins protruding outward (radial direction) from the center of theheat-exchanging honeycomb structure 20 in FIG. 5.

Next, the following describes the heat/acoustic wave conversioncomponent 1 in FIG. 3 in details.

FIG. 11A is a cross-sectional view of the heat/acoustic wave conversioncomponent 1 in FIG. 3 in a plane perpendicular to the penetratingdirection of the cells 14 of the heat/acoustic wave conversion component1.

As shown in FIG. 11A, the heat/acoustic wave conversion component 1includes a plurality of cells 14, each being a thin-tube like throughhole, that are partitioned and defined by a partition wall 11 (See FIG.3 as well for this point), and the partition wall 11 as a whole is thensurrounded with a circumferential wall 13. The circumferential wall 13may be made of the same material as that of the partition wall 11.

As described above, hydraulic diameters HDs of the cells 14 are one ofthe important factors to generate acoustic waves by self-inducedoscillations, and so the average hydraulic diameter HD of the pluralityof cells 14 in the heat/acoustic wave conversion component 1 has a verysmall value of 0.4 mm or less. Such cells with a very small averagehydraulic diameter HD can realize a sufficient thermoacoustic effectfrom the heat/acoustic wave conversion component 1. Conversely if theaverage hydraulic diameter HD of the plurality of cells 14 is largerthan 0.4 mm, a very small thermoacoustic effect only can be realized,and then it becomes difficult to obtain sufficient amount of electricpower and cold heat from the power generation system 1000 in FIG. 1 andthe cold heat generation system 2000 in FIG. 2.

Herein, for a larger thermoacoustic effect, it is advantageous to formas many as possible of the cells having a small hydraulic diameter HD asstated above. In other words, a larger open frontal area at the endfaces of the heat/acoustic wave conversion component 1 is moreadvantageous. The heat/acoustic wave conversion component 1 has a highopen frontal area at each end face that is 60% or more, from which alarge thermoacoustic effect can be achieved. On the other hand, if theopen frontal area is less than 60%, the number of cells contributing tothe thermoacoustic effect is too small, and so a very largethermoacoustic effect cannot be achieved therefrom.

Herein, if the open frontal area is too large, this means too manyhollows in the heat/acoustic wave conversion component 1 and so degradesthe durability and strength of the heat/acoustic wave conversioncomponent 1 as a whole. Then, the open frontal area of the heat/acousticwave conversion component 1 is suppressed to be 93% or less. Actually ifthe open frontal area exceeds 93%, damage on the heat/acoustic waveconversion component 1 due to thermal distortion and twisting (thermalstress) resulting from impacts of generated acoustic waves and atemperature difference at both ends of the heat/acoustic wave conversioncomponent 1 cannot be ignored.

In this way, the open frontal area at the end faces of the heat/acousticwave conversion component 1 that is 60% or more and 93% or less canachieve adequate balance between a sufficient thermoacoustic effect andsufficient durability/strength. The open frontal area of 80% or more and93% or less is preferable in the open frontal area of 60% or more and93% or less.

The open frontal area can be obtained by taking an image of a crosssection perpendicular to the penetrating direction by a microscope, anddetermining the material-part area S1 and the gap-part area S2 from thetaken image of the cross section. Then the open frontal area can beobtained as S2/(S1+S2) based on S1 and S2.

In the heat/acoustic wave conversion component 1, the plurality of cells14 have hydraulic diameters HDs of the plurality of cells 14 in a planeperpendicular to the penetrating direction of the cells 14, which aredifferent in accordance with each cell, and distribution of hydraulicdiameters HDs of the plurality of cells 14 has relative standarddeviation that is 2% or more and 30% or less. Herein, the relativestandard deviation is obtained, in a population including a plurality ofdata values each having one numerical value, by dividing the standarddeviation of the plurality of data values by an arithmetic average ofthe plurality of data values. As is clear from this definition, thisrelative standard deviation is a dimensionless value. This relativestandard deviation is called a variation coefficient as well, and is anamount representing the degree of variations of the numerical valuesamong a plurality of data values. The following briefly describes thereason why the plurality of cells 14 should have such variations in thedistribution of hydraulic diameters HDs.

In general, it can be considered that acoustic waves are generated by athermoacoustic effect, more strictly speaking because a temporal flow(movement) of the working fluid in at least a part of the cells of thehoneycomb structure serving as a heat/acoustic wave conversion componenttriggers compression/expansion of the working fluid due to exchange ofheat with the partition wall, which leads to occurrence of oscillationsof the working fluid (see the above description referring to FIG. 1 forsuch occurrence of oscillations due to compression/expansion). Forinstance, if working fluid flows from the outside of the honeycombstructure into the cells at an end part on the high-temperature side ofthe honeycomb structure for some reason, then such a flow inducesoscillations of the working fluid and starts heat/acoustic waveconversion.

Actually in order to start heat/acoustic wave conversion at aheat/acoustic wave conversion component, JP-A-2005-253240 proposes togive acoustic waves as a starter to the heat/acoustic wave conversioncomponent so as to induce acoustic waves by the heat/acoustic waveconversion component. Herein, if a structure to give acoustic waves as astarter is provided separately, then the configuration of the powergeneration system will be complicated. As a result, many powergeneration systems based on a thermoacoustic effect avoid having such astructure, and are configured to start heat/acoustic wave conversionsimply by giving a temperature difference at both ends of theheat/acoustic wave conversion component.

Note here that working fluid moves in various directions in themicroscopic sense in a tube accommodating the honeycomb structure (e.g.,in the looped tube as in FIG. 1). Such moving directions are at random,so that it has a state where no flow (movement) of the working fluidexists on average. Such random movement of the working fluid is calledtypically disturbance, and such disturbance includes a flow (movement)of the working fluid flowing into cells at an end part of the honeycombstructure on the high-temperature side, which can be considered as atrigger to start heat/acoustic wave conversion. Herein, even when theworking fluid moves to flow into cells at an end part of the honeycombstructure on the high-temperature side, the working fluid does notoscillate sufficiently and thus no acoustic waves are generated iftemperature gradient (that is obtained by dividing a temperaturedifference by the length of the honeycomb structure) of theheat/acoustic wave conversion component, due to the temperaturedifference at both end parts of the heat/acoustic wave conversioncomponent, is insufficient. However, if the temperature gradient isincreased gradually, then acoustic waves will be generated at a certainthreshold or more (see Patent Document 3, for example). Patent Document3 suggests particularly in paragraph [0038] that a smaller through holeof the honeycomb structure means a lower value of the threshold.

For this reason, it can be said that, in a honeycomb structure having aplurality of cells, a smaller average size of the cells (typicallyhydraulic diameter HD) is more advantageous for startability ofheat/acoustic wave conversion. However, it is still extremelynon-obvious, even if the result of Patent Document 3 is taken intoconsideration, that which distribution is advantageous for thestartability among various distributions of the hydraulic diameters HDsthat have substantially the same average of the hydraulic diameters HDsof the plurality of cells.

It appears that the distribution of hydraulic diameters HDs that hasmore uniform hydraulic diameters HDs more easily causes heat/acousticwave conversion (in other words, heat/acoustic wave conversion starts ata lower temperature gradient) as a whole of the plurality of cells. Anactual experiment (see Examples described later), however, showed thatheat/acoustic wave conversion was more easily generated in thedistribution of hydraulic diameters HDs with a certain degree ofvariations than in the distribution of hydraulic diameters HDs withnearly uniform hydraulic diameter HD values. It was further found,however, that too large variations then led to difficulty to causeheat/acoustic wave conversion. More specifically, it was found that whenthe hydraulic diameters HDs of the plurality of cells in a planeperpendicular to the cell penetrating direction has relative standarddeviation that is 2% or more and 30% or less, then startability ofheat/acoustic wave conversion is high (see Examples described later).

Although the definite reason for that is unknown, for example, thefollowing qualitative reasons can be considered. Firstly, for the lowerlimit of the numerical range as stated above, the following reason canbe considered. While the magnitude of speed of working fluid indisturbance has distribution to some extent, the magnitude of speed ofworking fluid that is appropriate to start heat/acoustic wave conversionalso may differ to a certain degree in accordance with the hydraulicdiameters HDs of the cells. Then, variations of hydraulic diameters HDsof cells to a certain degree can increase the probability to startheat/acoustic wave conversion at least any of the cells (in other words,it is easier to take disturbance), which may be a cause of the presenceof the lower limit of the numerical range. On the other hand, the upperlimit of the numerical range as stated above may be present because, ifvariations in distribution of hydraulic diameters HDs are too large,acoustic waves will be generated in only a small part of cells havingsmall hydraulic diameters HDs, and hardly generated as a whole of theplurality of cells.

Considering these circumstances, in the heat/acoustic wave conversioncomponent 1 in FIG. 11A, the distribution of hydraulic diameters HDs ofthe plurality of cells 14 has relative standard deviation that is 2% ormore and 30% or less. This can improve the startability of heat/acousticwave conversion in the heat/acoustic wave conversion component 1.

In order to schematically show the presence of variations of hydraulicdiameters HDs among the plurality of cells 14, FIG. 11A includes anenlarged view of a regular hexagonal region A and a regular hexagonalregion B each including six triangular cells 14 in the cross section ofthe heat/acoustic wave conversion component 1. Both of the regularhexagonal region A and the regular hexagonal region B are a regularhexagonal-shaped segment having the same area and shape, and the crosssection of the heat/acoustic wave conversion component 1 is made up ofthe collection of these regular hexagonal regions (for this reason, sucha regular hexagonal region, including the regular hexagonal region A andthe regular hexagonal region B, may be called regular hexagonal regions15 except when the inside of the regular hexagonal region A and theinside of the regular hexagonal region B are compared). Note here that,strictly speaking, an outer-edge part of the regular hexagonal region incontact with the circumferential wall does not have a complete regularhexagonal shape, and a part of the regular hexagonal shape is omitted.

In each regular hexagonal region, six cells 14 are arranged so as tosurround the center of the regular hexagonal region. Herein, the sixcells 14 included in the regular hexagonal region A have the samecross-sectional area and shape, and the six cells 14 included in theregular hexagonal region B also have the same cross-sectional area andshape. However, the six cells 14 included in the regular hexagonalregion A have a larger cross-sectional area than that of the six cells14 included in the regular hexagonal region B, and accordingly the cells14 included in the regular hexagonal region A have a larger hydraulicdiameter HD.

Two regular hexagonal regions of the regular hexagonal region A and theregular hexagonal region B are described above as an example. As isfound from this example also, the hydraulic diameter HD of the cells 14in each regular hexagonal region has one value determined in accordancewith the regular hexagonal region in the cross section of theheat/acoustic wave conversion component 1, and a plurality of types ofregular hexagonal regions having mutually different hydraulic diametersHD of the cells 14 are mixed in the cross section of the heat/acousticwave conversion component 1. This yields the state, in the cross sectionof the heat/acoustic wave conversion component 1 as a whole, theplurality of cells 14 of the heat/acoustic wave conversion component 1have variations of hydraulic diameters HDs.

Herein, as in a thickness T of the partition wall 11 in the regularhexagonal region A and a thickness T′ of the partition wall 11 in theregular hexagonal region B of FIG. 11A, the partition wall 11 betweenneighboring cells 14 in each regular hexagonal region has one thicknessvalue in accordance with the corresponding regular hexagonal region, andregular hexagonal regions of different types (as described above, typesare determined in accordance with the hydraulic diameters HDs) havedifferent thickness of the partition wall 11 in the regular hexagonalregions. Then, the partition wall 11 between two neighboring cells 14belonging to two neighboring regular hexagonal regions also has onevalue in accordance with the combination of the types of the twoneighboring regular hexagonal regions (types are determined inaccordance with the hydraulic diameters HDs), so that the partition wall11 has a different thickness in accordance with the combination of thetypes. As a result, there is realized in the heat/acoustic waveconversion component 1 that thickness of the partition wall 11 betweenneighboring cells has variations among all pairs of neighboring cells inthe heat/acoustic wave conversion component 1. As such variations ofthickness of the partition wall 11 between neighboring cells, thedistribution of thickness of the partition wall preferably has relativestandard deviation that is 3% or more and 22% or less, in view ofimprovement of startability of heat/acoustic wave conversion.

FIG. 11B is a conceptual diagram showing division of the cross sectionof a heat/acoustic wave conversion component using unit segments.

FIG. 11B shows the state where the cross section of the heat/acousticwave conversion component 1 in FIG. 11A is divided into a plurality ofunit segments with a unit segment 16. This unit segment 16 is arectangular region having a length Si in a horizontal direction(left-right direction) that is 1 mm and a length S2 in a verticaldirection (upper-lower direction) that is 1 mm.

When the cross section of the heat/acoustic wave conversion component 1is divided into a plurality of unit segments, as is clear from FIG. 11B,some of the plurality of unit segments include the cross section of thecircumferential wall 13. Remaining unit segments obtained by removingsuch unit segments including the cross section of the circumferentialwall 13 from the plurality of unit segments are called inside unitsegments in the following. For instance, the unit segment indicated withnumber “16” in FIG. 11B does not include the circumferential wall 13 atall, and so this is one of the inside unit segments. The following mayrefer to each of the inside unit segments in FIG. 11B as an inside unitsegment 16.

Corresponding to the existence of variations of hydraulic diameters HDsamong the plurality of cells 14, there is realized in the heat/acousticwave conversion component 1 that open frontal areas of the inside unitsegments have variations among all of the inside unit segments 16. Assuch variations of open frontal areas of the inside unit segments 16,the distribution of the open frontal areas of the inside unit segments16 preferably has relative standard deviation that is 7% or more and 40%or less, in view of improvement of startability of heat/acoustic waveconversion.

Such hydraulic diameters HDs, thickness of the partition wall 11 andopen frontal areas of the inside unit segments 16, each havingvariations, can be obtained by taking an image of a cross sectionperpendicular to the penetrating direction by a microscope, andmeasuring the area and the size of the cells 14, thickness of thepartition wall 11 and the like in the taken image of the cross section.

The variations of characteristic amounts of the plurality of cells 14,the partition wall 11 and the inside unit segment 16 of theheat/acoustic wave conversion component 1 are described above, and thefollowing describes features of the heat/acoustic wave conversioncomponent 1 other than the variation of the characteristic amounts.

Let that L denotes the length between both end faces of theheat/acoustic wave conversion component 1, the heat/acoustic waveconversion component 1 has a ratio HD/L of the hydraulic diameter HD asstated above to the length L that is 0.005 or more and less than 0.02.If HD/L is less than 0.005, the heat/acoustic wave conversion component1 is too long as compared with the hydraulic diameter HD. Then workingfluid in each cell of the heat/acoustic wave conversion component 1 willbe less affected from a temperature difference between both ends of theheat/acoustic wave conversion component. In this case, heat exchangebetween the working fluid in each cell and the partition wall 11 is notsufficient and so a sufficient thermoacoustic effect cannot be obtained.On the other hand, if HD/L is 0.02 or more, then heat/acoustic waveconversion component 1 is too short as compared with the hydraulicdiameter HD. In this case, heat is transmitted through the partitionwall 11 from the high-temperature side heat exchanger 2 side to thelow-temperature side heat exchanger 3 side in the heat/acoustic waveconversion component 1 before heat exchange between the working fluid ineach cell and the partition wall 11 becomes sufficient. As a result, asufficient thermoacoustic effect still cannot be obtained. Then, theheat/acoustic wave conversion component 1 is configured to have theratio HD/L of 0.005 or more and less than 0.02, and so heat exchangebetween the working fluid in each cell and the partition wall 11 issufficient. As a result, the heat/acoustic wave conversion component 1can have a sufficient thermoacoustic effect.

In the heat/acoustic wave conversion component of the present invention,cells in a plane perpendicular to the penetrating direction of the cellsmay have shapes that are various polygons, such as triangles,quadrangles, pentagons and hexagons as well as ellipses (including aperfect circle shape), where triangles, quadrangles and hexagons andtheir combinations are preferable. As shown in FIG. 11A, it isparticularly preferable to arrange triangle cells 14 periodically insuch a perpendicular plane.

Such triangular cells 14 are particularly preferable because, amongvarious polygonal shapes and elliptical cell shapes, triangular cellshapes are the most suitable for the arrangement of a lot of cells whileminimizing the thickness of the partition wall. Note here that, in thecase of a honeycomb structure to load catalyst for exhaust purificationto remove fine particles from exhaust gas of automobiles, if their cellshave corners at acute angles, fine particles easily accumulate at thecorners unfortunately. Then, such a honeycomb structure does not havetriangular cell shapes in many cases, although it can have such a shapein principle. On the other hand, in the case of a honeycomb structure toexert a thermoacoustic effect, such a problem does not happen to workingfluid (gas such as rare gas) causing self-induced oscillations, and sotriangular cell shapes, which are the most suitable to arrange a lot ofcells, can be used positively.

To simplify the description on variations, FIG. 11A shows regulartriangular-shaped cells 14 having corners at an acute angle, andactually the cells 14 have a triangular shape with curved corners, andthese corners have a curvature radius of 0.02 mm or more and 0.1 mm orless. Such a curvature radius of 0.02 mm or more means a gently curvedshape, and so it can sufficiently resist an impact acting to crush thecells 14. This is based on the same reason for the shape of a hole suchas a tunnel, i.e., a rounded shape is more resistant to an externalforce from the surrounding than an angular shape. On the other hand, ifthe curved part is too large, then the partition wall 11 close to thecorners of the cells is thick, and accordingly a part of the throughholes as the cells 14 contributing to the thermoacoustic effect can bereduced. Then, the curvature radius is set at 0.1 mm or less, whereby ahigh thermoacoustic effect also can be kept at the same time.

The curvature radius at the corners of the cells 14 can be measured bytaking an enlarged photo of the cells 14 in a cross sectionperpendicular to the penetrating direction and based on thecross-sectional shapes of the cells 14.

The material making up the heat/acoustic wave conversion component 1preferably has low heat conductivity of 5 W/mK or less. If the heatconductivity is larger than 5 W/mK, heat is transmitted through thepartition wall 11 from the high-temperature side heat exchanger 2 sideto the low-temperature side heat exchanger 3 side before heat exchangebetween the working fluid in each cell and the partition wall 11 becomessufficient. As a result, a sufficient thermoacoustic effect may not beobtained. On the other hand, such low heat conductivity of 5 W/mK orless leads to sufficient heat exchange between the working fluid in eachcell and the partition wall 11, and so a sufficient thermoacousticeffect can be obtained. Heat conductivity of 1.5 W/mK or less isparticularly preferable in the heat conductive of 5 W/mK or less. If theheat conductivity is too small, then the end face of the heat/acousticwave conversion component 1 on the high-temperature side heat exchanger2 side only has a high temperature locally, meaning a failure totransmit heat to the wall face in the cells and so the difficulty togenerate a thermoacoustic effect. Then, heat conductivity of at least0.01 W/mK is preferable.

The heat conductivity can be obtained by a temperature gradient method(steady method). Specifically, the heat conductivity can be obtained asfollows. Firstly, a plate-shaped test sample is cut out from a targetfor the heat conductivity measurement, and such a plate-shaped testsample is sandwiched between spacers whose heat conductivity is known(e.g., made of metals, such as copper and stainless steel). Then, oneside thereof is heated to 30° C. to 200° C., and the other side iscooled to 20 to 25° C., whereby a certain temperature difference isgiven in the thickness direction of the test sample. Then, the heat flowrate transmitted is obtained by the temperature gradient in the spacers,and this heat flow rate is divided by the temperature difference tocalculate the heat conductivity.

The following describes a method for manufacturing the monolithicheat/acoustic wave conversion component 1 in FIG. 11A. The followingdescribes the case where the heat/acoustic wave conversion component 1is made of a ceramic material.

Firstly, binder, surfactant, pore former, water and the like are addedto a ceramic raw material to prepare a forming raw material. The ceramicraw material preferably includes one or two or more in combination of acordierite forming raw material, a silicon carbide-cordierite basedcomposite material, aluminum titanate, silicon carbide, asilicon-silicon carbide based composite material, alumina, mullite,spinel, lithium aluminum silicate, and Fe—Cr—Al based alloy. Among them,a cordierite forming raw material is preferable. Herein the cordieriteforming raw material is a ceramic raw material formulated to have achemical composition in the range of 42 to 56 mass % of silica, 30 to 45mass % of alumina and 12 to 16 mass % of magnesia, and forms cordieriteafter firing. The ceramic raw material preferably is contained to be 40to 90 mass % with reference to the forming raw material as a whole.

Exemplary binder includes methyl cellulose, hydroxypropoxyl cellulose,hydroxyethylcellulose, carboxymethylcellulose, or polyvinyl alcohol.Among them, methyl cellulose and hydroxypropoxyl cellulose arepreferably used together. The content of the binder is preferably 2 to20 mass % with reference to the forming raw material as a whole.

The content of water is preferably 7 to 45 mass % with reference to thefoaming raw material as a whole.

Exemplary surfactant used includes ethylene glycol, dextrin, fatty acidsoap, or polyalcohol. They may be used alone or in combination of two ormore types. The content of the surfactant is preferably 5 mass % or lesswith reference to the forming raw material as a whole.

The pore former is not limited especially as long as it forms pores byfiring. Exemplary pore former includes starch, foamable resin, waterabsorbable resin or silica gel. The content of the pore former ispreferably 15 mass % or less with reference to the forming raw materialas a whole.

Next, a kneaded material is prepared by kneading the forming rawmaterial. A method for preparing a kneaded material by kneading theforming raw material is not limited especially. For instance, a kneaderor a vacuum pugmill may be used for this purpose.

Next, the kneaded material is extruded, whereby a honeycomb formed bodyis prepared, including a partition wall defining a plurality of cells.For the extrusion, a die having a shape in accordance with the hydraulicdiameter HD of each cell, the open frontal area, the shape of theheat/acoustic wave conversion component 1, the cell shape, and theperiod of the cells as stated above is preferably used. A preferablematerial of the die is cemented carbide having wear resistance. Valuesof the hydraulic diameter HD of each cell, the open frontal area, or thelike of the honeycomb formed body are determined, preferably whileconsidering contraction generated during drying and firing describedlater as well.

Herein the heat/acoustic wave conversion component 1 in FIG. 11A havinga very small hydraulic diameter HD of each cell and having a large openfrontal area (having large cell density) as stated above to exert alarger thermoacoustic effect cannot be manufactured by simply using anextrusion method as it is (i.e., by simply executing a similarmanufacturing method using a different die to form high-density pores)that is used for a conventional honeycomb structure to load catalyst forexhaust purification, which is free from such constraints, due to thefollowing two problems.

The first problem is that, during extrusion, kneaded material extrudedat a high temperature adheres to the holes in a forming die, whicheasily generates clogging. This problem is mentioned by Patent Document3 also in paragraph [0021].

The second problem is that a die used for a honeycomb structure as inthe heat/acoustic wave conversion component 1 of FIG. 11A having a verysmall hydraulic diameter HD of each cell and having a large open frontalarea (having large cell density) inevitably includes a very thin andminute part (typically a part of about 0.3 mm in thickness). Then, sucha minute part often is damaged (e.g., is torn) by viscous frictionduring kneaded material extrusion.

Then, the manufacturing method of the heat/acoustic wave conversioncomponent 1 has the following configuration to solve these two problems.

For the first problem, prior to the extrusion using a die (hereinaftercalled a real die) corresponding to the heat/acoustic wave conversioncomponent 1 having the hydraulic diameter of each cell that is 0.4 mm orless and the open frontal area that is 60% or more and 93% or less,i.e., having a very small hydraulic diameter of each cell and having alarge open frontal area (having large cell density), a kneaded materialis extruded using another die (hereinafter called a dummy die) having avery small thickness of ribs that is 0.04 mm or more and 0.09 mm orless. The “thickness of ribs” here refers to the thickness of thepartition wall of the honeycomb formed body, and means a slit width ofthe die. Each slit is a hole to discharge the kneaded material and is todetermine the shape of each partition wall part at the honeycombstructure to be manufactured. In the following, the “thickness of ribs”means the slit width. The extrusion using such a dummy die can removebeforehand the component of the kneaded material that tends to be acause of the clogging. Then extrusion by a real die is performed for thekneaded material subjected to the extrusion, whereby clogging as statedabove can be suppressed.

The second problem is solved by reducing viscosity of the kneadedmaterial used for extrusion greatly as compared with the viscosity of akneaded material used for a conventional honeycomb structure to loadcatalyst for exhaust purification so as to reduce the viscous frictionwhile keeping the range of a shape-holding property (i.e. the shape ofthe formed body is not distorted) of the formed body of theheat/acoustic wave conversion component 1 during extrusion. To reducethe viscosity of kneaded material while satisfying the condition to keepa shape-holding property in this way, the ratio of water in the kneadedmaterial has to be more strictly controlled than in the manufacturing ofa conventional honeycomb structure to load catalyst for exhaustpurification (i.e., keeping an error between the control target of thewater ratio and the actual water ratio in a very narrow range).Specifically, the ratio of water in the kneaded material is 40 to 42parts by mass with reference to 100 parts by mass of the kneadedmaterial solid component that is used to manufacture the heat/acousticwave conversion component 1, while the ratio of water in the kneadedmaterial is 25 to 35 parts by mass with reference to 100 parts by massof the kneaded material solid component that is used to manufacture aconventional honeycomb structure to load catalyst for exhaustpurification. When the ratio of water in the kneaded material increases,then viscosity of the kneaded material decreases and adequatefluctuations occur in the shape of the formed body of the heat/acousticwave conversion component 1. This leads to another advantageous effectthat self-induced oscillations of acoustic waves likely occur.

The following describes a die that is used to prepare a honeycomb formedbody (i.e., extrusion) in the present embodiment. For ease ofexplanation, the following mainly describes the case where cells have aquadrangular shape.

FIG. 12 is a perspective view showing the appearance of a die that isused to prepare a honeycomb formed body in the present embodiment, andFIG. 13 is a perspective view showing the appearance of the die in FIG.12 that is viewed from the opposite side of FIG. 12. FIG. 14 is anenlarged plan view showing a part of the surface of the die in FIG. 12,and FIG. 15 schematically shows a cross section of the die of FIG. 14taken along the line A-A′.

As shown in FIGS. 12 to 15, a die 301 includes a second plate-shapedpart 303, and a first plate-shaped part 307 made of tungsten carbidebased cemented carbide. Herein the second plate-shaped part 303 is madeof at least one type selected from the group consisting of iron, steelmaterials, aluminum alloy, copper alloy, titanium alloy and nickelalloy, and this second plate-shaped part 303 includes a back hole 305 tointroduce the forming raw material of the honeycomb formed body. Thefirst plate-shaped part 307 includes a hole part 311 that is incommunication with the back hole 305, and also includes a slit 309 thatis in communication with the hole part 311 and defines a cell block 313.This first plate-shaped part 307 includes a first layer 307 a disposedon the second plate-shaped part 303 side and a second layer 307 bdisposed on the first layer 307 a. Herein, the hole part 311 is open atboth of the faces of the first layer 307 a, and the slit 309 is open atboth of the faces of the second layer 307 b. FIG. 15 shows the statewhere the hole part 311 has an open end 311 a at a first bonding face310 that agrees with an open end 305 a of the back hole 305 at thesecond bonding face. Such a configuration of the die 301 is to lengthenthe life of the die as described later.

The die 301 preferably has a thickness of 4 to 10 mm. If the thicknessis less than 4 mm, the die may be broken during forming. If thethickness is more than 10 mm, pressure loss is high during forming of ahoneycomb structure, meaning difficulty in forming in some cases.

The second plate-shaped part 303 includes a plate-shaped member made ofat least one type selected from the group consisting of iron, steelmaterials, aluminum alloy, copper alloy, titanium alloy and nickelalloy. Herein steel materials are at least one type selected from thegroup consisting of stainless steel, dies steel and high-speed steel.Among these materials, steel materials are preferable as the material ofthe second plate-shaped part 303, and stainless steel is morepreferable.

In the present application, “at least one type selected from the groupconsisting of iron, steel materials, aluminum alloy, copper alloy,titanium alloy and nickel alloy” may be referred to as “free-machiningmaterial”. The free-machining material is a material that can be easilyground as compared with tungsten carbide based cemented carbide. Sincethe second plate-shaped part 303 does not include the slit 309, wearingis less problematic in the second plate-shaped part 303 than in thefirst plate-shaped part 307. Since the second plate-shaped part 303 ismade of free-machining material, the second plate-shaped part 303 hasexcellent workability as compared with tungsten carbide based cementedcarbide. Further the cost for free-machining material is lower than thatof the tungsten carbide based cemented carbide, and so the manufacturingcost can be reduced.

Stainless steel that is one type of the materials available as thesecond plate-shaped part 303 may be well-known stainless steel. Forinstance, it may be SUS304, SUS303 and the like. The size of the secondplate-shaped part 303 is not limited especially, and it may have adesired size depending on the purpose. Herein when the secondplate-shaped part 303 has a circular plate shape, the diameter of thecircular plate (diameters of one face and the other face) is preferably20 to 40 mm. The thickness of the second plate-shaped part 303 ispreferably 2 to 8 mm. If the thickness is less than 2 mm, it maygenerate deformation and breakage due to stress from forming resistance,and if the thickness is more than 8 mm, forming resistance is excessive,meaning difficulty in extrusion of the formed body.

As described above, the second plate-shaped part 303 includes the backhole 305 to introduce the forming raw material, and the back hole 305 isa through hole (a hole that is open at both faces of the secondplate-shaped part 303) to introduce the forming raw material. When thehoneycomb structure is formed using this die 301, the forming rawmaterial for the honeycomb structure is introduced from the back hole305. The back hole 305 may have any shape as long as it can guide theintroduced forming raw material to the hole part 311 and the slit 309,and the back hole 305 preferably has a circular shape in a cross sectionorthogonal to the flowing direction of the forming raw material(thickness direction of the second plate-shaped part). The open end ofthe back hole 305 preferably has a diameter of 0.15 to 0.45 mm, where0.25 to 0.40 mm is more preferable. Such a back hole 305 can be formedby machine processing, such as electrochemical machining (ECM),electrical discharge machining (EDM), laser processing and drillprocessing, for example. Among these methods, electrochemical machining(ECM) is preferable because ECM can form the back hole 305 effectivelyand precisely. The space in the back hole is preferably in around-pillar shape. In this case, the diameter (diameter of the backhole) in a cross section orthogonal to the flowing direction of theforming raw material (thickness direction of the second plate-shapedpart) in the back hole can have a constant value. In this case, thediameter of the back hole is equal to the diameter of the open end ofthe back hole at the second bonding face. The number of back holes isnot limited especially, which can be decided appropriately depending onthe shape of the honeycomb structure to be manufactured, for example.When the cells have a triangular shape, then the back holes preferablyare disposed at all of the positions corresponding to the intersectionsof the honeycomb partition wall, and when the cells have a quadrangularshape, then the back holes are preferably disposed at alternateintersections of the honeycomb partition wall in a staggered pattern.

The first plate-shaped part 307 includes a plate-shaped member made oftungsten carbide based cemented carbide. The width of the slit 309 isvery narrow as compared with the diameter of the back hole 305. Thismeans that, when the forming raw material is extruded, pressure in theback hole 305 is increased and stress concentrates on the slit 309,which often leads to problems of wearing and deformation, for example.Then, the first plate-shaped part 307 is made of tungsten carbide basedcemented carbide that is a material having wear resistance. Herein,“tungsten carbide based cemented carbide (cemented carbide)” is an alloywhere tungsten carbide and a bonding material are sintered. The bondingmaterial is preferably at least one type of metal selected from thegroup consisting of cobalt (Co), iron (Fe), nickel (Ni), titanium (Ti)and Chromium (Cr). Such tungsten carbide based cemented carbide hasespecially excellent wear resistance and mechanical strength.

The size of the first plate-shaped part 307 is not limited especially,and it may have a desired size in accordance with the purpose. Hereinwhen the first plate-shaped part 307 has a circular plate shape, thediameter of the circular plate is preferably 20 to 40 mm. When the firstplate-shaped part 307 and the second plate-shaped part 303 have acircular plate shape, then the diameter of the first plate-shaped part307 is 90 to 100% of the diameter of the second plate-shaped part 303.The thickness of the first plate-shaped part 307 is preferably 0.3 to1.2 mm, where 0.5 to 0.9 mm is more preferable. The thickness of thefirst plate-shaped part 307 is preferably 0.05 to 2 times the thicknessof the second plate-shaped part 303.

As described above, the first plate-shaped part 307 includes the firstlayer 307 a disposed on the second plate-shaped part 303 side and thesecond layer 307 b disposed on the first layer 307 a. Since the die 301at the first plate-shaped part includes these two layers of the firstlayer 307 a and the second layer 307 b, stress during extrusion can bemitigated, and so breakage can be prevented. The first layer 307 a andthe second layer 307 b may be made of the same type of materials or ofdifferent types of materials.

In this way, the first layer 307 a is one layer making up the firstplate-shaped part 307, and is disposed on the second plate-shaped part303 side. Herein, the first layer 307 a includes the hole part 311. Thefirst layer 307 a preferably is a layer made of cemented carbide havingVickers hardness of 2,000 to 3,000 HV and having the Young's modulus of600 to 800 GPa. When the first layer 307 a has such Vickers hardness andYoung's modulus, it can be a layer having hardness and toughness thatcan resist the stress applied to the hole part 311. Then problems suchas breakage of the first plate-shaped part 307, which may result fromthe stress from the forming raw material flowing into the hole part 311from the back hole 305, can be prevented, and so the life of the die canbe lengthened. The hole part 311 is open at both faces of the firstlayer 307 a.

The first layer 307 a preferably has Vickers hardness of 2,000 to 3,000HV, where 2,000 to 2,200 HV is more preferable. With such predeterminedVickers hardness, the first layer 307 a can have hardness so as toresist the stress from the ceramic raw material flowing into the holepart 311 from the back hole 305. Then wearing of the hole part 311 canbe prevented. If the Vickers hardness of the first layer 307 a is lessthan 2,000 HV, wearing may occur due to the lack of strength. If theVickers hardness of the first layer 307 a exceeds 3,000 HV, it is toohard, and so the first layer 307 a may easily break. The first layer 307a preferably has the Young's modulus of 600 to 800 GPa, where 600 to 700GPa is more preferable. This can prevent breakage of the first layer 307a. If the Young's modulus of the first layer 307 a is less than 600 GPa,the toughness is too small, which may cause problems such as breakage.If the Young's modulus exceeds 800 GPa, the toughness is too large,which may lead to the risk of deformation of the hole part 311. When thehoneycomb structure is formed using a die having the deformed hole part311, then distortion occurs at the honeycomb structure and theformability deteriorates.

As described above, the second layer 307 b is one layer making up thefirst plate-shaped part 307, and is disposed on the first layer 307 a.The second layer 307 b includes the slit 309, and the slit 309 is openat both faces of the second layer 307 b. Herein “both faces of thesecond layer 307 b” mean both faces including the face of the secondlayer 307 b in contact with (bonded to) the first layer 307 a and theface on the opposite side (rear side) of the face in contact with thefirst layer 307 a. In FIG. 15, the discharge port of the forming rawmaterial at the slit 309 is indicated as an open end 309 a of the slit309. The second layer 307 b preferably has Vickers hardness of 500 to3,000 HV and the Young's modulus of 400 to 700 GPa. When the secondlayer 307 b has such Vickers hardness and Young's modulus, it can be alayer having sufficient hardness and toughness that can resist thestress applied to the slit 309. Then deformation and wearing of the slit309 can be prevented.

The second layer 307 b preferably has Vickers hardness of 500 to 3,000HV, where Vickers hardness of 2,000 to 3,000 HV is more preferable. SuchVickers hardness of the layer can suppress wearing of the second layer307 b. If the Vickers hardness of the second layer 307 b is less than500 HV, wearing may occur easily due to the lack of hardness. If theVickers hardness exceeds 3,000 HV, the second layer 307 b may easilybreak.

The second layer 307 b preferably has the Young's modulus of 400 to 700GPa, where the Young's modulus of 500 to 700 GPa is more preferable.Such Young's modulus of the second layer 307 b makes the layer hard tobreak. If the Young's modulus of the second layer 307 b is less than 400GPa, problems such as breakage easily occur due to too small toughness.If the Young's modulus exceeds 700 GPa, then the toughness is too large,and so the second layer 307 b easily is deformed.

It is preferable that, in the die 301, the Vickers hardness and theYoung's modulus of the second layer 307 b are larger than the Vickershardness and the Young's modulus of the first layer 307 a. That is, itis preferable that the Vickers hardness of the second layer 307 b islarger than the Vickers hardness of the first layer 307 a, and theYoung's modulus of the second layer 307 b is larger than the Young'smodulus of the first layer 307 a. In such a relationship, the secondlayer 307 b including the slit 309 hardly becomes worn, and the firstlayer 307 a including the hole part 311 hardly breaks. Then, the life ofthe die can be lengthened more due to the second layer 307 b suppressingwearing and the first layer 307 a suppressing breakage.

In the die 301, it is preferable that the Vickers hardness of the secondlayer 307 b is larger than the Vickers hardness of the first layer 307 aby 1,000 to 2,500 HV, and the Young's modulus of the second layer 307 bis larger than the Young's modulus of the first layer 307 a by 50 to 300GPa. Then, the first plate-shaped part 307 can have the second layer 307b having wear resistance and the first layer 307 a having high toughnessreliably, and so the life of the die can be lengthened.

The thickness of the first layer 307 a is preferably 0.1 to 5 mm, andthe thickness of the first layer 307 a is 0.2 to 5 mm more preferably.Such a range of the thickness of the first layer 307 a can suppresswearing of the second plate-shaped part effectively. If the thickness ofthe first layer 307 a is less than 0.1 mm, the second plate-shaped parteasily becomes worn. If the thickness of the first layer 307 a exceeds 5mm, pressure during extrusion may increase too high due to such a thickdie.

The thickness of the second layer 307 b is preferably 0.3 to 4 mm, andthe thickness is 1 to 4 mm more preferably. Such a range of thethickness of the second layer 307 b can suppress deformation of thehoneycomb structure after extrusion. If the thickness of the secondlayer 307 b is less than 0.3 mm, the honeycomb structure after extrusionmay be deformed, which may lead to wearing and deformation at the secondlayer 307 b. If the thickness of the second layer 307 b exceeds 4 mm,then the second layer 307 b is too thick and so the depth of the slit(the length of the slit in the extruding direction of the forming rawmaterial) is too large, so that pressure during extrusion becomes toohigh. Further, a part surrounded by the slit is extremely long and thin,and the part may be torn due to friction with kneaded material. In orderto prevent such events, a deep slit is not allowed. On the other hand,when the slit is shallow in an adequate degree, then relativefluctuations in the slit depth increase between a plurality of slits. Asa result, the honeycomb structure after extrusion also can have adequatefluctuations in shape, and so self-induced oscillations of acousticwaves easily occur.

As stated above, the first plate-shaped part 307 includes the slit 309that is in communication with the hole part 311 and is to form theforming raw material. The slit 309 is a gap (cut) formed in the firstplate-shaped part 307. The forming raw material introduced from the backhole 305 enters the slit 309 in the die, and then the forming rawmaterial is pushed out from the open end 309 a of the slit 309, wherebya formed body in a honeycomb shape can be formed.

As stated above, the slit 309 is open at both faces of the second layer307 b. Although the slit 309 may be formed at the second layer 307 bonly, it is preferable that the slit is formed at the first layer 307 aas well. When it is formed at the first layer 307 a, the slit 309 formedat the second layer 307 b is extended to the first layer side so as tobe formed at the first layer 307 a preferably. In this case, the slit309 at the first layer 307 a is formed at the face of the first layer307 a in contact with the second layer 307 b. Then in this case, thedepth of the slit 309 is larger than the thickness of the second layer307 b. It is preferable that the depth of the slit 309 is 0.3 to 1.0 mm,where 0.4 to 0.8 mm is more preferable. It is preferable that the depthof the slit 309 at a part extended to the first layer side is 0.1 to 0.5mm, where 0.2 to 0.5 mm is more preferable. This can form a formed bodyof a favorable honeycomb shape. It is preferable that the width of theslit 309 is 0.03 to 0.05 mm, where 0.04 to 0.05 mm is more preferable.

As described above, the first layer 307 a of the first plate-shaped part307 includes the hole part 311 therein, where this hole part 311 is incommunication with the back hole 305 formed at the second plate-shapedpart 303 and the slit 309 formed at the first plate-shaped part 307. Thehole part 311 is a through hole as well that is formed at the firstlayer 307 a of the first plate-shaped part 307. That is, the hole part311 is a through hole that is open at the face of the second layer 307 bon the side in contact with the second plate-shaped part 303 (the firstbonding face 310 of the first plate-shaped part 307) and is open at theface of the second layer 307 b in contact with the first layer 307 a(the other face 307 ba of the second layer). As shown in FIG. 15, thefirst bonding face 310 is a face of the first plate-shaped part 307 thatis bonded (in contact with) to the second plate-shaped part 303. Such ahole part 311 allows a forming raw material introduced from the backhole 305 formed at the second plate-shaped part 303 to pass through thehole part 311 and enter the slit 309. Then the forming raw material ispushed out from the open end 309 a of the slit 309, whereby a honeycombshaped formed body (honeycomb structure) can be formed. It is preferablethat the depth h of the hole part 311 (see FIG. 15) is 0.1 to 4 mm,where 0.2 to 3 mm is more preferable. Such a range of the depth h of thehole part 311 can suppress wearing at the second plate-shaped part 303effectively. If the depth h of the hole part is less than 0.1 mm, thestrength of the first plate-shaped part 307 easily deteriorates duringextrusion of the forming raw material. If the depth h of the hole partexceeds 4 mm, it tends to be difficult to form the hole part byprocessing the first plate-shaped member during preparation of the die.Herein, the depth h of the hole part 311 is a distance from the firstbonding face 310 of the first plate-shaped part 307 to the other face307 ba of the second layer 307 b as shown in FIG. 15. Herein, the depthof the hole part 311 equals the thickness of the first layer 307 a. Itis preferable that the diameter of the open end 311 a of the hole part311 is 0.15 to 0.4 mm, where 0.2 to 0.4 mm is more preferable. The holepart 311 may be formed by machine processing, such as electrochemicalmachining (ECM), electrical discharge machining (EDM), laser processingand drill processing, for example. Among these methods, electrochemicalmachining (ECM) is preferable because it can form the hole part 311effectively and precisely. The space in the hole part 311 is preferablyin a round-pillar shape. In this case, the diameter (diameter of thehole part 311) in a cross section orthogonal to the flowing direction ofthe forming raw material (thickness direction of the first plate-shapedpart) in the hole part 311 can have a constant value. At this time, thediameter of the hole part 311 is equal to the diameter of the open end311 a of the hole part at the first bonding face 310. The number of thehole parts 311 is preferably the same number as that of the back holes.

As shown in FIG. 15, the die 301 is formed so that the diameter dl ofthe open end 311 a (circle) of the hole part 311 at the first bondingface 310 is the same size as that of the diameter D1 of the open end 305a (circle) of the back hole at the second bonding face 306. As shown inFIG. 15, the second bonding face 306 is a face of the secondplate-shaped part 303 that is bonded to (in contact with) the firstplate-shaped part 307. The open end 311 a of the hole part 311 at thefirst bonding face 310 is an inlet part of the through hole (inflow partof the forming raw material) that is open at the first bonding face 310.The open end 305 a of the back hole 305 at the second bonding face 306is an outlet part (outlet part of the forming raw material) on thesecond bonding face 306 side that is open at the second bonding face 306of the back hole 305. As the forming raw material passes through thisoutlet part, it is then supplied to the hole part 311.

Herein it is preferable that the die includes a retainer plateconfiguration to fix the die for extrusion.

FIG. 16 shows an example of the retainer plate configuration.

In the retainer plate configuration of FIG. 16, the forming raw materialis pushed out in the direction of the downward arrow in FIG. 16. At thistime, a rear retaining part 403 can adjust the amount of kneadedmaterial that flows in. A die 401 is fixed by a retainer 402, and aforming raw material that is pushed out from a gap 405 between the die401 and the retainer 402 defines a circumferential part of a honeycombformed body 404 while being adjusted by an inclined face 406 and anopposed face 407.

FIG. 17 shows another example of the retainer plate configuration thatis different from FIG. 16.

In a retainer plate configuration 550 of FIG. 17, the forming rawmaterial is pushed out in the direction of the downward arrow in FIG.17. This retainer plate configuration 550 includes a back hole 553 tosupply a forming raw material, a die 554 having a slit 552 to push outthe forming raw material and a retaining plate 555 that is disposeddownstream of the die 554. The die 554 includes an inside part 571 and acircumference part 572. The inside part 571 protrudes toward thedownstream (downward in FIG. 17) to define a step height 575 with thecircumference part 572, and this inside part 571 is provided with a slit573 to form a honeycomb structure. The circumference part 572 is thenprovided with a slit 574 that is shorter than the slit 573. Between thedie 554 and the retaining plate 555, a gap part 557 to form the outerwall of the honeycomb structure is formed. Herein a retaining jig 558and a rear-retaining plate 559 are holders to set the die 554 and theretaining plate 555.

During extrusion using the retainer plate configuration 550 in FIG. 17,the forming raw material is pushed out from the upstream side of the die554 (above in FIG. 17) toward the downstream via the die 554 by anextruder (not shown). The forming raw material 561 that is pushed outfrom the slit 573 at the inside part 571 of the die 554, the slit 573being open on the downstream side, is formed to be a honeycomb structureincluding a lot of cells. On the other hand, the forming raw material561 that is pushed out from the slit 574 at the circumference part 572of the die 554 has a crushed honeycomb shape by the action at the gappart 557, and changes the traveling direction from the pushing-outdirection to the direction toward the step height 575 and changes againthe traveling direction to the pushing-out direction at the place wherethe retaining plate 555 is open so as to form the outer wall surroundingthe cells.

FIG. 18 shows still another example of the retainer plate configuration.FIG. 19 shows a further example of the retainer plate configuration thatis different from FIG. 18.

The retainer plate configuration in FIG. 18( a) includes a die 604having slits 602 to form the periodic arrangement of regular trianglesas shown in FIG. 18( b). This die 604 is to form a honeycomb structurehaving a regular triangular cell shape, which is fixed by a retainingplate 605. Herein the slits 602 are in communication with back holes603. In this retainer plate configuration, the shape (dimensions) of thehoneycomb formed body to be formed is determined by the length L1 of theslits 602, the length L2 that is obtained by subtracting the height of astep height 615 from the length L1 of the slits 602, the width W of theslits 602 and the distance d between the retaining plate 605 and thestep height 615.

FIG. 19 shows a further example of the retainer plate configuration thatis different from FIG. 18.

The retainer plate configuration in FIG. 19( a) includes a die 704having slits 702 to form the periodic arrangement of squares as shown inFIG. 19( b). This die 704 is to form a honeycomb structure having asquare cell shape, which is fixed by a retaining plate 705. Herein theslits 702 are in communication with back holes 703. In this retainerplate configuration also, the shape (dimensions) of the honeycomb formedbody to be formed is determined by the length L1 of the slits 702, thelength L2 that is a difference between the length L1 of the slits 702and the height of a step height 715, the width W of the slits 702 andthe distance d between the retaining plate 705 and the step height 715.

In both of the retainer plate configurations in FIG. 18 and FIG. 19, itis preferable that the length L1 of the slits 702 is 0.3 to 1.0 mm,where 0.4 to 0.8 mm is more preferable. Then it is preferable that thelength L2 as the difference is 0.1 to 0.5 mm.

The following continues the description on the following processing forthe honeycomb formed body that is obtained by the extrusion.

The thus obtained honeycomb formed body is dried before firing. A methodfor drying is not limited especially, and exemplary methods include anelectromagnetic wave heating method such as microwave heat-drying andhigh-frequency induction heating drying and an external heating methodsuch as hot air drying and superheated steam drying. After a certainamount of water may be dried by an electromagnetic wave heating method,followed by an external heating method to dry the remaining water. Inthis case, it is preferable that, after 30 to 90 mass % of water withreference to the water amount before drying is removed by anelectromagnetic heating method, followed by an external heating methodto reduce water amount to 3 mass % or less. A preferable electromagneticwave heating method includes induction heating drying, and a preferableexternal heating method includes hot air drying.

If the length of the honeycomb formed body in the cell penetratingdirection is not a desired length, it is preferable to cut both of theend faces (end parts) to have the desired length. Although a method forcutting is not limited especially, exemplary method includes a methodusing a circular saw cutter.

Next, the honeycomb formed body is fired. It is preferable to performcalcination before firing to remove the binder and the like. Thecalcination is preferably performed at 400 to 500° C. for 0.5 to 20hours in the ambient atmosphere. A method for calcination or firing isnot limited especially, and they may be performed using an electricfurnace, a gas furnace, or the like. As the firing conditions, it ispreferably heated at 1,300 to 1,500° C. for 1 to 20 hours in an inertatmosphere of nitrogen, argon, or the like when a silicon-siliconcarbide based composite material is used, for example. When anoxide-based material is used, it is preferably heated at 1,300 to 1,500°C. for 1 to 20 hours in an oxygen atmosphere.

Finally, if it is required to be a desired cross-sectional shape (e.g.,a circle as in FIG. 11A) of the heat/acoustic wave conversion component1, the circumferential part of the honeycomb formed body after thefiring step is cut as needed to correct the shape. Then, an outercoating material is applied to the circumferential face of the honeycombformed body after cutting, followed by drying, whereby a circumferentialwall 13 is formed. Herein, the outer coating material used may beslurry, for example, which is prepared by adding an additive such asorganic binder, foamable resin or dispersing agent to a raw materialincluding inorganic particles and colloidal oxide, to which water isadded, followed by kneading. Herein exemplary inorganic particlesinclude particles made of a ceramic material containing one or two ormore in combination of cordierite, alumina, aluminum titanate, siliconcarbide, silicon nitride, mullite, zirconia, zirconium phosphate andtitania, or particles of Fe—Cr—Al-based metal, nickel-based metal andsilicon (metal silicon)-silicon carbide based composite materials.Exemplary colloidal oxide includes silica sol and alumina sol. A methodfor applying the outer coating material is not limited especially, andfor example, the coating material may be coated with a rubber spatula,for example, while rotating the honeycomb formed body after cutting on awheel.

Through such steps, the heat/acoustic wave conversion component 1 inFIG. 11A finally is completed.

Next, the following describes a method for manufacturing thehigh-temperature side heat exchanger 2 in FIG. 3.

The heat-exchanging honeycomb structure 20 in the high-temperature sideheat exchanger 2 of FIG. 3 can be manufactured by a manufacturing methodsimilar to the method for manufacturing the monolithic heat/acousticwave conversion component 1 in FIG. 11A as stated above, other than thatmixture of carbon powder (e.g., graphite powder) with SiC powder is usedas the ceramic raw material and a die suitable for a honeycomb formedbody having a relatively large hydraulic diameter HD of cells is used asthe die for extrusion.

To manufacture this heat-exchanging honeycomb structure 20, for example,including a Si impregnated SiC composite material as a main component,it is preferable that a kneaded material prepared by mixing SiC powderwith carbon powder and kneading for adjustment is formed to be ahoneycomb formed body, then drying and sintering processing areperformed thereto, and then molten silicon (Si) is impregnated in thishoneycomb formed body. Such processing can form a configuration wherecoagulation of metal Si (metal silicon) surrounds the surface of SiCparticles after the sintering processing, and SiC particles are mutuallybonded via metal Si. Such a configuration can achieve high heatdurability and heat conductivity in spite of the dense configurationwith small porosity.

In addition to the molten silicon (Si), other metals such as Al, Ni, Cu,Ag, Be, Mg, and Ti may be used for impregnation. In this case, aftersintering, coagulation of metal Si (metal silicon) and other metals usedfor impregnation surrounds the surface of SiC particles, and SiCparticles are mutually bonded via metal Si and other metals used forimpregnation in the formed configuration. Such a configuration also canachieve high heat durability and heat conductivity in spite of the denseconfiguration with small porosity.

As the outer coating material of the heat-exchanging honeycomb structure20 as well, particles of silicon (metal silicon)-silicon carbide basedcomposite material is preferably used for the same reason as statedabove, among the particles made of the materials as stated above as thecandidates of inorganic particles of the material of the outer coatingmaterial (the material of the bonding material of the heat/acoustic waveconversion component 1).

It is preferable to perform slit formation processing to form a slit inthe cell penetrating direction at the circumferential wall formed by theapplication of the outer coating material. When the slit formationprocessing is performed, a heat resistant metal plate 21 d and a fin 21e may be formed when the high-temperature side annular tube 21 ismanufactured as described below.

The high-temperature side annular tube 21 on the high-temperature sideheat exchanger 2 in FIG. 3 is prepared by forming a material of highheat resistance to be an annular shape (herein, the annular shape suchthat a part of the wall face on the center side is partially omitted sothat, when being coupled with the heat-exchanging honeycomb structure20, a part of the circumferential wall of the heat-exchanging honeycombstructure 20 is exposed in the high-temperature side annular tube). Sucha material of high heat resistance is not limited especially, andspecific examples include metal such as stainless steel and copper ofhigh heat resistance and ceramic materials (e.g., those listed as thematerials of the heat/acoustic wave conversion component 1 in FIG. 11Aand the heat-exchanging honeycomb structure 20).

The high-temperature side heat exchanger 2 in FIG. 3 is completedbasically by assembling the heat-exchanging honeycomb structure 20 at acenter part that is a hole at the annular shape of the high-temperatureside annular tube 21.

Next the following describes a method for manufacturing thelow-temperature side heat exchanger 3 in FIG. 3. When a conventionallyknown heat exchanger is used as the low-temperature side heat exchanger3, a method for manufacturing such a conventionally known heat exchangercan be used. When the device having the same configuration as that ofthe high-temperature side heat exchanger 2 stated above is used as thelow-temperature side heat exchanger 3, the same manufacturing method asthat of the high-temperature side heat exchanger 2 as stated above canbe used.

As other members of the heat/acoustic wave conversion unit 100 in FIG.3, e.g., the metal member 32, the housing 100 a, and the interferencemember 1 a, those conventionally known can be used, and they can bemanufactured by a conventionally known method.

EXAMPLES

The following describes the present invention more specifically by wayof examples, and the present invention is by no means limited to theseexamples.

Example 1

In Example 1, cordierite forming raw material was used as the ceramicraw material. Then 35 parts by mass of dispersing medium, 6 parts bymass of organic binder, and 0.5 parts by mass of dispersing agent wereadded to 100 parts by mass of the cordierite forming raw material,followed by mixing and kneading to prepare a kneaded material. Thecordierite forming raw material used included 38.9 parts by mass of talcof 3 μm in average particle size, 40.7 parts by mass of kaolin of 1 μmin average particle size, 5.9 parts by mass of alumina of 0.3 μm inaverage particle size, and 11.5 parts by mass of boehmite of 0.5 μm inaverage particle size. Herein the average particle size refers to amedian diameter (d50) in the particle distribution of each raw material.

Water was used as the dispersing medium. Hydroxypropylmethylcellulosewas used as the organic binder. Ethylene glycol was used as thedispersing agent.

Next, the thus obtained kneaded material was extruded using a die, sothat a plurality of honeycomb formed bodies each including triangularcells and having a hexagonal overall shape were prepared. During thisextrusion, prior to the extrusion using a regular die corresponding tothe heat/acoustic wave conversion component of Example 1, the kneadedmaterial was extruded using a dummy die of about 0.07 mm in ribthickness. Then, using the kneaded material after the extrusion usingthis dummy die, extrusion using the real die was executed. At this time,the ratio of water in the kneaded material used for the extrusion usingthe real die was strictly controlled in the kneaded material componentso that it was 41 parts by mass (error was within ±1 part by mass) withreference to 100 parts by mass of the kneaded material solid component.

At this time, the retainer plate configuration in FIG. 18 was used asthe retainer plate configuration for the die. In this retainer plateconfiguration, the length L1 (see FIG. 18) of the slit was 0.5 mm, andthe length L2 (see FIG. 18) obtained by subtracting the height of thestep height from the slit length L1 was 0.2 mm. Then, the width W (seeFIG. 18) of the slit was 0.05 mm, and the distance d (see FIG. 18)between the retaining plate and the step height was 0.5 mm.

Then, this honeycomb formed body was dried by a microwave dryer, andthen was dried completely by a hot-air drier, and then both end faces ofthe honeycomb formed body were cut so as to adjust the length of thehoneycomb formed body in the cell penetrating direction. Such ahoneycomb formed body was dried by a hot-air drier, and then was firedat 1,445° C. for 5 hours.

Finally, the circumferential part of the honeycomb formed body after thefiring step was cut as needed to correct the shape to be a round-pillarshape. Then, an outer coating material was applied to thecircumferential face of the honeycomb formed body after cutting,followed by drying, whereby a circumferential wall 13 was formed.Herein, the outer coating material used was slurry prepared by addingorganic binder, foamable resin and dispersing agent to a raw materialincluding cordierite particles and silica sol, to which water was addedand kneaded. As a method for applying the outer coating material, thecoating material was coated with a rubber spatula, for example, whilerotating the honeycomb formed body after cutting on a wheel.

Through these steps, the heat/acoustic wave conversion component ofExample 1 was finally completed.

For the thus completed heat/acoustic wave conversion component ofExample 1, the hydraulic diameters HDs of cells, the open frontal areasat end faces and the thickness of the partition wall between neighboringcells were measured at a cross section in a plane (perpendicular plane)perpendicular to the cell penetrating direction. Then, this crosssection was divided into a plurality of unit segments while setting therectangular region of 1 mm in length and 1 mm in width as a unitsegment, and then the open frontal areas were measured for the insideunit segments that were the unit segments obtained by removing the unitsegments including the cross section of the circumferential wall fromthe plurality of unit segments.

The hydraulic diameters HDs of the cells were obtained as follows. Thatis, an enlarged photo of the cross section of the heat/acoustic waveconversion component in the perpendicular plane was taken, and any 100cells were selected in this enlarged photo of the cross section. Then,the hydraulic diameter HD of each of the 100 cells was calculated by theexpression to define the hydraulic diameter: HD=4×S/C, where S denotesthe cross-sectional area of the cell and C denotes the perimeter of thissection. The thickness of the partition wall between neighboring cellswas obtained by selecting any 100 pairs of neighboring cells in thisenlarged photo of the cross section, and measuring the thickness of thepartition wall between the neighboring cells of each pair. The openfrontal areas of the inside unit segments were obtained by selecting any100 inside unit segments in this enlarged photo of the cross section,and measuring the open frontal area of each of these 100 inside unitsegments.

Herein, in this measurement, the selected 100 cells, the selected 100pairs of neighboring cells, and the selected 100 inside unit segmentsrepresent all of the cells, all of the pairs of neighboring cells, andall of the inside unit segments in this cross section.

The open frontal area was obtained by taking an image of the crosssection in the perpendicular plane by a microscope, and determining thematerial-part area S1 and the gap-part area S2 from the image taken ofthe cross section. Then the open frontal area was obtained as S2/(S1+S2)based on S1 and S2. This is common to the calculation of the openfrontal area at the cross section as a whole and to the calculation ofthe open frontal at each inside unit segment. Herein, the open frontalarea at the cross section as a whole is considered to be equal to theopen frontal area at the end faces, and so the open frontal area at thecross section as a whole is used as the open frontal area at the endfaces.

Based on the measurement values obtained through the measurement asstated above, the following five types of parameters were obtained. Thefollowing five types of parameters include ones that are not independentmutually and change together with other parameters, but such parametersalso are described for the sake of descriptions.

(1) Average of hydraulic diameters HDs of cells for 100 cells of theheat/acoustic wave conversion component in the plane (perpendicularplane) perpendicular to the cell penetrating direction,

(2) Open frontal area of the cross section as a whole of theheat/acoustic wave conversion component in the above perpendicular plane(the same as the open frontal area at the end faces),

(3) Relative standard deviation of the distribution of hydraulicdiameters HDs among the 100 cells of the heat/acoustic wave conversioncomponent as stated above (obtained by dividing the standard deviationof the distribution by an arithmetic average of the distribution),

(4) Relative standard deviation (definition is the same as in (3)) ofthe distribution of thickness of the partition wall between neighboringcells among the 100 pairs of neighboring cells of the heat/acoustic waveconversion component, and

(5) Relative standard deviation (definition is the same as in (3)) ofthe distribution of open frontal areas of the inside unit segments amongthe 100 inside unit segments of the heat/acoustic wave conversioncomponent.

The following experiment was conducted using this heat/acoustic waveconversion component of Example 1.

The experiment was as follows. Firstly, the heat/acoustic waveconversion component of Example 1 was assembled in the power generationsystem 1000 of FIG. 1, instead of the heat/acoustic wave conversioncomponent 1. Then, water at 60° C. was allowed to flow into thelow-temperature side heat exchanger 3 so as to let the end of theheat/acoustic wave conversion component on the side of thelow-temperature side heat exchanger 3 keep the temperature at 60° C. Inthis state, exhaust gas from an automobile was allowed to flow into thehigh-temperature side heat exchanger 2 of the heat/acoustic waveconversion component. Then, the temperature of the exhaust gas from theautomobile flowing in was allowed to rise little by little from about60° C. At this time, using a microphone or the like as the energyconverter of the power generation system 1000 of FIG. 1, the amount ofelectric power generated at the energy converter was monitored, wherebythe temperature where acoustic waves started to be generated (startingtemperature of heat/acoustic waves (° C.)) was obtained. Then, the ratioof the absolute temperature where the heat/acoustic wave conversion wasstarted (starting temperature of heat/acoustic waves (° C.)+273° C.) tothe absolute temperature (in the units of K) at the end on thelow-temperature side heat exchanger 3 side, i.e., 333 K (60° C.+273° C.)was calculated.

Example 2 and Comparative Example 1

Heat/acoustic wave conversion components as Example 2 and ComparativeExample 1 were manufactured by the same manufacturing method as that ofthe manufacturing method of Example 1 as stated above except that a dieused for extrusion was different, where these heat/acoustic waveconversion components were different from Example 1 only in the value ofthe average of hydraulic diameters HDs of the cells among the five typesof parameters as stated above. These Example 2 and Comparative Example 1had different values of average of hydraulic diameters HDs of the cells,but had the same degree of variations of hydraulic diameters HDs in thedistribution of hydraulic diameters HDs of the cells as that ofExample 1. That is, the values of hydraulic diameters HDs change for theentire data as a whole.

Examples 3, 4 and Comparative Examples 2, 3

Heat/acoustic wave conversion components as Examples 3, 4 andComparative Examples 2, 3 were manufactured by the same manufacturingmethod as that of the manufacturing method of Example 1 as stated aboveexcept that a die used for extrusion was different, where theseheat/acoustic wave conversion components were different from Example 1only in the value of the open frontal area of the cross section as awhole of the heat/acoustic wave conversion component among the fivetypes of parameters as stated above.

Then, the experiment similar to those for Example 1 was conducted forthese Examples 3, 4 and Comparative Examples 2, 3.

Examples 5, 6 and Comparative Examples 4, 5

Heat/acoustic wave conversion components as Examples 5, 6 andComparative Examples 4, 5 were manufactured by the same manufacturingmethod as that of the manufacturing method of Example 1 as stated aboveexcept that a die used for extrusion was different, where theseheat/acoustic wave conversion components were different from Example 1only in the values of the relative standard deviation of thedistribution of hydraulic diameters HDs, the relative standard deviationof the distribution of thickness of partition wall, and the relativestandard deviation of the distribution of open frontal areas of theinside unit segments. These Examples 5, 6 and Comparative Examples 4, 5were different from Example 1 only in the value of the relative standarddeviation of the distribution of hydraulic diameters HDs, but had thesame value of average of the hydraulic diameters HDs of the cells andvalue of the open frontal area of the cross section as a whole of theheat/acoustic wave conversion component as those of Example 1. That is,these Examples 5, 6 and Comparative Examples 4, 5 had differentdistribution of hydraulic diameters HDs and such distribution of openfrontal areas of the inside unit segments while keeping the average ofthe hydraulic diameters HDs and the open frontal area of the crosssection as a whole of the heat/acoustic wave conversion component.

The following Table 1 shows the experimental results of Examples 1 to 6and Comparative Examples 1 to 5 as explained above, together with thevalues of these parameters. The following Table 1 describes the averageof the partition wall thickness between neighboring cells among 100pairs of neighboring cells as well, and the average of the partitionwall thickness was 0.05 mm for any Example and Comparative Example.

TABLE 1 Open frontal area Relative standard Relative standard Relativestandard Average of Average of of cross section deviation of deviationof deviation of Ratio of absolute partition wall cell hydraulic as awhole of heat/ distribution of cell distribution distribution of opentemperature where thickness diameters HDs acoustic wave con- hyraulicdiameters of partition frontal areas at heat/acoustic wave (mm) (mm)version component (%) HDs wall thickness inside unit segments conversionstarts Ex. 1 0.05 0.25 74 5 6 10 1.2 Ex. 2 0.05 0.4 74 5 6 8 1.6 Comp.Ex. 1 0.05 0.45 74 5 6 8 2.2 Comp. Ex. 2 0.05 0.25 55 4 5 9 2.5 Ex. 30.05 0.25 60 4 5 9 1.25 Ex. 4 0.05 0.25 93 5 6 11 1.1 Comp. Ex. 3 0.050.25 95 5 6 8 — Comp. Ex. 4 0.05 0.25 74 1.5 1 2 2.3 Ex. 5 0.05 0.25 742 3 7 1.3 Ex. 6 0.05 0.25 74 30 22 40 1.25 Comp. Ex. 5 0.05 0.25 74 35 650 2.5

In Table 1, as is found from a comparison between Examples 1, 2 andComparative Example 1 having mutually different values of average of thehydraulic diameters HDs, Examples 1 and 2 had a smaller ratio of thestarting temperature of heat/acoustic wave conversion than ComparativeExample 1. This shows that the value of the average of hydraulicdiameters HDs of 0.4 mm or less is desirable to improve the startabilityof heat/acoustic wave conversion.

In Table 1, as is found from a comparison between Examples 3, 4 andComparative Examples 2, 3 having mutually different values of openfrontal area of the cross section as a whole of the heat/acoustic waveconversion component, Examples 3 and 4 had a smaller ratio of thestarting temperature of heat/acoustic wave conversion than ComparativeExample 2. For Comparative Example 3, since damage occurred during theexperiment, the experiment was stopped, so that the final result was notobtained for the ratio of the starting temperature of heat/acoustic waveconversion. Presumably this was due to the shortage of strength anddurability because the open frontal area was too high. This shows thatthe value of the open frontal area of the cross section as a whole(value of the open frontal area at the end faces) of the heat/acousticwave conversion component of 60% or more and 93% or less is desirable toimprove the startability of heat/acoustic wave conversion while keepingsufficient strength.

In Table 1, as is found from a comparison between Examples 5, 6 andComparative Examples 4, 5 having mutually different values of relativestandard deviation of the distribution of hydraulic diameters HDs (andrelative standard deviation of the distribution of thickness ofpartition wall between neighboring cells or relative standard deviationof the distribution of open frontal areas of the inside unit segments),Examples 5 and 6 had a smaller ratio of the starting temperature ofheat/acoustic wave conversion than Comparative Examples 4, 5. This showsthat the value of the relative standard deviation of the distribution ofhydraulic diameters HDs of 2% or more and 30% or less is desirable toimprove the startability of heat/acoustic wave conversion.

At this time, it is found from a comparison between Examples 5, 6 andComparative Examples 4, 5 that the distribution of thickness ofpartition wall between neighboring cells preferably has relativestandard deviation of 3% or more and 22% or less to improve thestartability of heat/acoustic wave conversion. Then, it is found thatthe distribution of open frontal areas of the inside unit segmentspreferably has relative standard deviation of 7% or more and 40% or lessto improve the startability of heat/acoustic wave conversion.

The above describes the experimental results about startability ofheat/acoustic wave conversion, and in order to confirm the effect of thetwo configurations during extrusion as stated above, the followingexperiment for extrusion was conducted for reference experiment.

(1) Extrusion for a heat/acoustic wave conversion component wasattempted by the same manufacturing method as that of Example 1 exceptthat the dummy die used had a rib thickness of 0.09 mm.

(2) Extrusion for a heat/acoustic wave conversion component wasattempted by the same manufacturing method as that of Example 1 exceptthat the dummy die used had a rib thickness of 0.10 mm.

(3) Extrusion for a heat/acoustic wave conversion component wasattempted by the same manufacturing method as that of Example 1 exceptthat the dummy die used had a rib thickness of 0.04 mm.

(4) Extrusion for a heat/acoustic wave conversion component wasattempted by the same manufacturing method as that of Example 1 exceptthat the dummy die used had a rib thickness of 0.03 mm.

(5) Extrusion for a heat/acoustic wave conversion component wasattempted by the same manufacturing method as that of Example 1 exceptthat the kneaded material used included water at the ratio in thekneaded material that was about 43 parts by mass (error was within ±1part by mass) with reference to 100 parts by mass of the kneadedmaterial solid component.

(6) Extrusion for a heat/acoustic wave conversion component wasattempted by the same manufacturing method as that of Example 1 exceptthat the kneaded material used included water at the ratio in thekneaded material that was about 39 parts by mass (error was within ±1part by mass) with reference to 100 parts by mass of the kneadedmaterial solid component.

As a result, forming was enabled without problems in (1) and (3), but in(2) and (6), clogging of the kneaded material occurred in the holes inthe forming die, and so forming failed. In (4), considerable pressurewas required for extrusion by the dummy die, which showed thepossibility of damage in the die, and so the experiment was stopped. In(5), the formed body obtained by the extrusion was deformed easily dueto the self weight, and a desired shape was not obtained.

Considering these results together with the successful result ofextrusion in Example 1, it can be found that pre-extrusion is preferablyperformed using a dummy die having a rib thickness of 0.04 mm or moreand 0.09 mm or less and the ratio of water in the kneaded material ispreferably 40 to 42 parts by mass with reference to 100 parts by mass ofthe kneaded material solid component.

The present invention is favorably used in a system that effectivelyuses heat from exhaust gas of automobiles or the like to generateelectric power and cold heat.

DESCRIPTION OF REFERENCE NUMERALS

-   1: heat/acoustic wave conversion component-   1 a: interference member-   2, 2′, 2A, 2A′: high-temperature side heat exchanger-   3: low-temperature side heat exchanger-   4: looped tube-   4′: looped tube-   5: resonant tube-   5′: transmission tube-   6: energy converter-   7: acoustic-wave generation part-   11: partition wall-   12: bonding part-   12′: bonding part-   13: circumferential wall-   14: cell-   15: regular hexagonal region-   16: (inside) unit segment-   20: heat-exchanging honeycomb structure-   20′: heat-exchanging honeycomb structure-   20 a: partition wall-   20 b: circumferential wall-   20 c: slit-   20 d: cell-   20 s: contact face-   21: high-temperature side annular tube-   211: high-temperature side annular tube-   212: high-temperature side annular tube-   2110: in-tube honeycomb structure-   2120: in-tube honeycomb structure-   21 a: inflow port-   21 b: outflow port-   21 c: heat-receiving region-   21 d: heat-resistant metal plate-   21 e: fin-   22, 23: honeycomb structure-   23′: metal mesh member-   22 a: metal outer tube-   23 a: metal mesh outer tube-   23 b: metalized layer-   30: mesh lamination body-   31: low-temperature side annular tube-   31 a: inflow port-   31 b: outflow port-   32: metal member-   301: die-   303: second plate-shaped part-   305: back hole-   305 a, 309 a, 311 a; open end-   306: second bonding face-   307: first plate-shaped part-   307 a: first layer-   307 b: second layer-   307 ba: other face of second layer-   309: slit-   310: first bonding face-   311: hole part-   313: cell block-   401: die-   402: retainer-   403: rear retaining part-   404: honeycomb formed body-   405: gap-   406: inclined face-   407: opposed face-   550: retainer plate configuration-   552: slit-   553: back hole-   554: die-   555: retaining plate-   557: gap part-   558: retaining jig-   559: rear-retaining plate-   561: extruded forming raw material-   571: inside part-   572: circumference part-   573, 574: slit-   575: step height-   602, 702: slit-   603, 703: back hole-   604, 704: die-   605, 705: retaining plate-   615, 715: step height-   100: heat/acoustic wave conversion unit-   200: heat/acoustic wave conversion unit-   100 a: housing-   1000: power generation system-   2000: cold heat generation system

What is claimed is:
 1. A heat/acoustic wave conversion component havinga first end face and a second end face, comprising a partition wall thatdefines a plurality of cells extending from the first end face to thesecond end face, inside of the cells being filled with fluid thatoscillates to transmit acoustic waves, the heat/acoustic wave conversioncomponent mutually converting heat exchanged between the partition walland the fluid and energy of acoustic waves resulting from oscillationsof the fluid, wherein the plurality of cells have an average ofhydraulic diameters HDs that is 0.4 mm or less, where each hydraulicdiameter HD is defined as HD=4×S/C, where S denotes an area of across-section of each cell in a plane perpendicular to the cellextending direction and C denotes a perimeter of the cross section, theheat/acoustic wave conversion component has an open frontal area at eachend face of 60% or more and 93% or less, and the plurality of cells havehydraulic diameters HDs thereof which are different in accordance witheach cell, and distribution of hydraulic diameters HDs of the pluralityof cells has relative standard deviation that is 2% or more and 30% orless.
 2. The heat/acoustic wave conversion component according to claim1, wherein pairs of mutually neighboring cells of the plurality of cellshave thickness of the partition wall between neighboring cells of eachpair which is different in accordance with each neighboring cells, anddistribution of thickness of the partition wall between the neighboringcells has relative standard deviation that is 3% or more and 22% orless.
 3. The heat/acoustic wave conversion component according to claim1, further comprising a circumferential wall that surrounds acircumferential face of the partition wall as a whole that defines theplurality of cells, wherein when the cross section of the heat/acousticwave conversion component in the plane is divided into a plurality ofunit segments each of which is a rectangular region of 1 mm in lengthand 1 mm in width, inside unit segments, which are remaining unitsegments obtained by removing unit segments including the cross sectionof the circumferential wall from the plurality of unit segments, haveopen frontal areas of the cells therein which are different inaccordance with each inside unit segment, and distribution of openfrontal areas of the cells in the inside unit segments has relativestandard deviation of 7% or more and 40% or less.
 4. A heat/acousticwave conversion unit, comprising the heat/acoustic wave conversioncomponent according to claim 1, in a state where inside of the pluralityof cells is filled with the fluid, when there is a temperaturedifference between a first end part on the first end face side and asecond end part on the second end face side, the heat/acoustic waveconversion component oscillating the fluid along the extending directionin accordance with the temperature difference and generating acousticwaves; and a pair of heat exchangers that are disposed in a vicinity ofthe first end part and the second end part of the heat/acoustic waveconversion component, respectively, the heat exchangers exchanging heatwith the both end parts to give a temperature difference between theboth end parts.
 5. A heat/acoustic wave conversion unit comprising: theheat/acoustic wave conversion component according to claim 1, in a statewhere inside of the plurality of cells is filled with the fluid, andwhen the fluid oscillates along the extending direction while receivingacoustic waves transmitted, the heat/acoustic wave conversion componentgenerating a temperature difference between a first end part on thefirst end face side and a second end part on the second end face side inaccordance with oscillations of the fluid; a heat exchanger that isdisposed in a vicinity of one of the first end part and the second endpart of the heat/acoustic wave conversion component, the heat exchangersupplying heat to the one end part or absorbing heat from the one endpart to keep a temperature at the one end part constant; and a hotheat/cold heat output unit that is disposed in a vicinity of the otherend part of the first end part and the second end part of theheat/acoustic wave conversion component that is on the opposite side ofthe one end part, the hot heat/cold heat output unit outputting hot heator cold heat obtained from exchanging of heat with the other end part sothat, in a state where the temperature of the one end part is keptconstant by the heat exchanger and when the heat/acoustic waveconversion component receives acoustic waves transmitted, the other endpart has a temperature difference in accordance with oscillations of thefluid due to transmission of the acoustic waves with reference to theone end part kept at the constant temperature.
 6. The heat/acoustic waveconversion component according to claim 2, further comprising acircumferential wall that surrounds a circumferential face of thepartition wall as a whole that defines the plurality of cells, whereinwhen the cross section of the heat/acoustic wave conversion component inthe plane is divided into a plurality of unit segments each of which isa rectangular region of 1 mm in length and 1 mm in width, inside unitsegments, which are remaining unit segments obtained by removing unitsegments including the cross section of the circumferential wall fromthe plurality of unit segments, have open frontal areas of the cellstherein which are different in accordance with each inside unit segment,and distribution of open frontal areas of the cells in the inside unitsegments has relative standard deviation of 7% or more and 40% or less.7. A heat/acoustic wave conversion unit, comprising the heat/acousticwave conversion component according to claim 2, in a state where insideof the plurality of cells is filled with the fluid, when there is atemperature difference between a first end part on the first end faceside and a second end part on the second end face side, theheat/acoustic wave conversion component oscillating the fluid along theextending direction in accordance with the temperature difference andgenerating acoustic waves; and a pair of heat exchangers that aredisposed in a vicinity of the first end part and the second end part ofthe heat/acoustic wave conversion component, respectively, the heatexchangers exchanging heat with the both end parts to give a temperaturedifference between the both end parts.
 8. A heat/acoustic waveconversion unit, comprising the heat/acoustic wave conversion componentaccording to claim 3, in a state where inside of the plurality of cellsis filled with the fluid, when there is a temperature difference betweena first end part on the first end face side and a second end part on thesecond end face side, the heat/acoustic wave conversion componentoscillating the fluid along the extending direction in accordance withthe temperature difference and generating acoustic waves; and a pair ofheat exchangers that are disposed in a vicinity of the first end partand the second end part of the heat/acoustic wave conversion component,respectively, the heat exchangers exchanging heat with the both endparts to give a temperature difference between the both end parts.
 9. Aheat/acoustic wave conversion unit, comprising the heat/acoustic waveconversion component according to claim 6, in a state where inside ofthe plurality of cells is filled with the fluid, when there is atemperature difference between a first end part on the first end faceside and a second end part on the second end face side, theheat/acoustic wave conversion component oscillating the fluid along theextending direction in accordance with the temperature difference andgenerating acoustic waves; and a pair of heat exchangers that aredisposed in a vicinity of the first end part and the second end part ofthe heat/acoustic wave conversion component, respectively, the heatexchangers exchanging heat with the both end parts to give a temperaturedifference between the both end parts.
 10. A heat/acoustic waveconversion unit comprising: the heat/acoustic wave conversion componentaccording to claim 2, in a state where inside of the plurality of cellsis filled with the fluid, and when the fluid oscillates along theextending direction while receiving acoustic waves transmitted, theheat/acoustic wave conversion component generating a temperaturedifference between a first end part on the first end face side and asecond end part on the second end face side in accordance withoscillations of the fluid; a heat exchanger that is disposed in avicinity of one of the first end part and the second end part of theheat/acoustic wave conversion component, the heat exchanger supplyingheat to the one end part or absorbing heat from the one end part to keepa temperature at the one end part constant; and a hot heat/cold heatoutput unit that is disposed in a vicinity of the other end part of thefirst end part and the second end part of the heat/acoustic waveconversion component that is on the opposite side of the one end part,the hot heat/cold heat output unit outputting hot heat or cold heatobtained from exchanging of heat with the other end part so that, in astate where the temperature of the one end part is kept constant by theheat exchanger and when the heat/acoustic wave conversion componentreceives acoustic waves transmitted, the other end part has atemperature difference in accordance with oscillations of the fluid dueto transmission of the acoustic waves with reference to the one end partkept at the constant temperature.
 11. A heat/acoustic wave conversionunit comprising: the heat/acoustic wave conversion component accordingto claim 3, in a state where inside of the plurality of cells is filledwith the fluid, and when the fluid oscillates along the extendingdirection while receiving acoustic waves transmitted, the heat/acousticwave conversion component generating a temperature difference between afirst end part on the first end face side and a second end part on thesecond end face side in accordance with oscillations of the fluid; aheat exchanger that is disposed in a vicinity of one of the first endpart and the second end part of the heat/acoustic wave conversioncomponent, the heat exchanger supplying heat to the one end part orabsorbing heat from the one end part to keep a temperature at the oneend part constant; and a hot heat/cold heat output unit that is disposedin a vicinity of the other end part of the first end part and the secondend part of the heat/acoustic wave conversion component that is on theopposite side of the one end part, the hot heat/cold heat output unitoutputting hot heat or cold heat obtained from exchanging of heat withthe other end part so that, in a state where the temperature of the oneend part is kept constant by the heat exchanger and when theheat/acoustic wave conversion component receives acoustic wavestransmitted, the other end part has a temperature difference inaccordance with oscillations of the fluid due to transmission of theacoustic waves with reference to the one end part kept at the constanttemperature.
 12. A heat/acoustic wave conversion unit comprising: theheat/acoustic wave conversion component according to claim 6, in a statewhere inside of the plurality of cells is filled with the fluid, andwhen the fluid oscillates along the extending direction while receivingacoustic waves transmitted, the heat/acoustic wave conversion componentgenerating a temperature difference between a first end part on thefirst end face side and a second end part on the second end face side inaccordance with oscillations of the fluid; a heat exchanger that isdisposed in a vicinity of one of the first end part and the second endpart of the heat/acoustic wave conversion component, the heat exchangersupplying heat to the one end part or absorbing heat from the one endpart to keep a temperature at the one end part constant; and a hotheat/cold heat output unit that is disposed in a vicinity of the otherend part of the first end part and the second end part of theheat/acoustic wave conversion component that is on the opposite side ofthe one end part, the hot heat/cold heat output unit outputting hot heator cold heat obtained from exchanging of heat with the other end part sothat, in a state where the temperature of the one end part is keptconstant by the heat exchanger and when the heat/acoustic waveconversion component receives acoustic waves transmitted, the other endpart has a temperature difference in accordance with oscillations of thefluid due to transmission of the acoustic waves with reference to theone end part kept at the constant temperature.